Catalyst filter comprising nano metallic catalyst sprayed on the surface of support
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B01J-023/22
B01J-023/42
B01J-023/44
B01J-023/06
B01J-023/34
B01J-035/06
B01J-023/28
B01J-035/04
B01J-037/02
B01D-053/86
출원번호
US-0227001
(2016-08-03)
등록번호
US-9844767
(2017-12-19)
우선권정보
KR-10-2015-0122097 (2015-08-28)
발명자
/ 주소
Jurng, Jongsoo
Kim, Min Su
Park, Eun Seuk
Jung, Hyoun Duk
Kim, Jin Young
출원인 / 주소
Korea Institute of Science and Technology
대리인 / 주소
NSIP Law
인용정보
피인용 횟수 :
0인용 특허 :
5
초록▼
Disclosed is a catalyst filter, which includes a catalyst support and a nano metallic catalyst sprayed to a surface of the catalyst support. The catalyst filter uses catalyst slurry prepared by using a particulate catalyst, in which a small amount of nano metallic catalyst exhibiting a catalyst perf
Disclosed is a catalyst filter, which includes a catalyst support and a nano metallic catalyst sprayed to a surface of the catalyst support. The catalyst filter uses catalyst slurry prepared by using a particulate catalyst, in which a small amount of nano metallic catalyst exhibiting a catalyst performance is sprayed to a surface of the catalyst support, different from an existing patent technique in which catalyst particles are formed and prepared as a support to consume a large amount of catalyst. Therefore, the specific surface area of the catalyst filter is not smaller than the specific surface area of the nano catalyst particles, and thus the catalyst filter may effectively remove and decompose ultra-low concentration gas-state contaminants in an indoor air.
대표청구항▼
1. A catalyst filter, comprising: a catalyst support; anda nano metallic catalyst dispersed onto a surface of the catalyst support,wherein a weight of the nano metallic catalyst per unit area of the catalyst filter is 300 g/m2 to 450 g/m2. 2. The catalyst filter according to claim 1, wherein the nan
1. A catalyst filter, comprising: a catalyst support; anda nano metallic catalyst dispersed onto a surface of the catalyst support,wherein a weight of the nano metallic catalyst per unit area of the catalyst filter is 300 g/m2 to 450 g/m2. 2. The catalyst filter according to claim 1, wherein the nano metallic catalyst is spray-coated onto the surface of the catalyst support. 3. The catalyst filter according to claim 1, wherein the nano metallic catalyst is sprayed onto the surface of the catalyst support to form a film layer. 4. The catalyst filter according to claim 1, wherein the catalyst support is any one of paper, cotton, and ceramic. 5. The catalyst filter according to claim 4, wherein the catalyst support is any one or any combination of any two or more selected from the group consisting of carbon paper, corrugated type carbon paper, carbon cloth, carbon felt, fibrous textile, cellulose pulp paper, non-woven fabric, honeycomb paper filter and cordierite. 6. The catalyst filter according to claim 1, wherein the nano metallic catalyst comprises a precious metal catalyst made of platinum or palladium, or a transition metal catalyst prepared by impregnating any one or any combination of any two or more of titanium dioxide (TiO2), silicon dioxide (SiO2) and aluminum oxide (Al2O3) with any one or any combination of any two or more of copper, manganese, iron, vanadium, molybdenum, cobalt, nickel and zinc. 7. The catalyst filter according to claim 6, wherein the nano metallic catalyst comprises a manganese oxide-titania catalyst or a vanadia-titania catalyst. 8. The catalyst filter according to claim 7, wherein the manganese oxide-titania catalyst comprises a catalyst in which manganese oxide is supported by titania particles, and comprises a specific surface area of 200 m2/g to 300 m2/g. 9. The catalyst filter according to claim 1, wherein the nano metallic catalyst is provided by 15 weight % to 30 weight %, on the basis of the weight of the catalyst filter. 10. A method of preparing a catalyst filter, comprising: spraying a nano metallic catalyst onto a surface of a catalyst support; anddistributing the nano metallic catalyst by regularly spreading the nano metallic catalyst onto the surface of the catalyst support, after the spraying,wherein the nano metallic catalyst is dispersed onto the surface of the catalyst support. 11. The method of preparing the catalyst filter according to claim 10, further comprising spraying the nano metallic catalyst using spray coating. 12. The method of preparing the catalyst filter according to claim 10, wherein the spraying of the nano metallic catalyst comprises spraying the nano metallic catalyst using compressed air. 13. The method of preparing the catalyst filter according to claim 10, further comprising: drying the catalyst support, after the spraying. 14. The method of preparing the catalyst filter according to claim 13, wherein the drying of the catalyst support is performed at a temperature of 40° C. to 70° C. for 2 to 10 hours. 15. The method of preparing the catalyst filter according to claim 13, further comprising: removing impurities after the drying of the catalyst support. 16. The method of preparing the catalyst filter according to claim 15, wherein the removing of the impurities is performed by blowing compressed air to the catalyst support. 17. The method of preparing the catalyst filter according to claim 10, further comprising: spraying and distributing the nano metallic catalyst onto another surface of the catalyst support and drying the nano metallic catalyst, after the nano metallic catalyst is sprayed and distributed onto the surface of the catalyst support and dried. 18. The method of preparing the catalyst filter according to claim 17, wherein the nano metallic catalyst is dried for 3 to 5 hours at the first surface and dried for 7 to 9 hours at the second surface. 19. The method of preparing the catalyst filter according to claim 10, further comprising: preparing a coating slurry comprising a nano metallic catalyst, before the spraying of the nano metallic catalyst,wherein the spraying of the nano metallic catalyst comprises spraying the coating slurry onto the catalyst support. 20. The method of preparing the catalyst filter according to claim 19, wherein the preparing of the coating slurry comprises: a) adding methyl cellulose to distilled water and stirring at 30° C. to 50° C. for 1 hour to 3 hours to form a slurry;b) adding bentonite to the slurry of the step (a) and stirring at 30° C. to 50° C. for 1 hour to 3 hours; andc) adding a nano metallic catalyst to the slurry of the step (b) and stirring at 30° C. to 50° C. for 1 hour to 3 hours. 21. The method of preparing the catalyst filter according to claim 19, wherein the coating slurry comprises a mixture of 15 wt % to 20 wt % of nano metallic catalyst, 8 wt % to 12 wt % of bentonite, 1 wt % to 2 wt % of methyl cellulose, and 65 wt % to 75 wt % of water.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (5)
Fukuda, Tsutomu; Fukuda, Masahiro; Fukuda, Masaaki; Yoko, Toshinobu; Takahashi, Masahide, Honeycomb carrier for exhaust gas clarification catalyst and method for production thereof.
Kezuka, Masamichi; Miyashita, Kiyoshi; Ogawa, Ryohei; Hishinuma, Akihiro, Photocatalyst containing metallic ultrafine particles and process for producing said photocatalyst.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.