The invention relates to a method for manufacturing composite particles, particularly composite particles based on titanium dioxide and carbonate, with the help of combined mixing, homogenization and precipitation in a pipeline mixer based on the rotor-stator principle. The method is based on an aqu
The invention relates to a method for manufacturing composite particles, particularly composite particles based on titanium dioxide and carbonate, with the help of combined mixing, homogenization and precipitation in a pipeline mixer based on the rotor-stator principle. The method is based on an aqueous suspension of a particulate base component (e.g. titanium dioxide), which is preferably produced in an intermediate vessel equipped with a high-speed agitator. At least one of the required precursor substances and/or a pH-controlling component for precipitating calcium carbonate, for example, is metered into the pipeline mixer, and the calcium carbonate is precipitated. The method can be operated as a continuous process or as a batch process and permits shorter production times. The composite particles produced display homogeneous dispersion of the precipitated particles and the particulate base component.
대표청구항▼
1. A method for manufacturing composite particles, containing at least one particulate base component and in-situ precipitated inorganic particles comprising: providing an aqueous suspension of the particulate base component;pumping the suspension through a pipeline mixer based on the rotor-stator p
1. A method for manufacturing composite particles, containing at least one particulate base component and in-situ precipitated inorganic particles comprising: providing an aqueous suspension of the particulate base component;pumping the suspension through a pipeline mixer based on the rotor-stator principle;metering into the pipeline mixer at least one dissolved or dispersed precursor compound and a pH-controlling component for producing the in-situ precipitated inorganic particles;wherein no gaseous reaction component is added to the pipeline mixer; andwherein the inorganic particles are predominantly precipitated in the pipeline mixer. 2. The method of claim 1, wherein the aqueous suspension of the particulate base component is produced in an intermediate vessel equipped with a high-speed agitator having a circumferential speed of at least 15 m/s or a specific agitator capacity of at least 30 W/m3. 3. The method of claim 1, wherein in the method is operated as a continuous process. 4. The method of claim 1, wherein in the method is operated in a circuit. 5. The method of claim 1, wherein the particulate base is titanium dioxide. 6. The method of claim 5, wherein the particulate base component comprises at least one extender. 7. The method of claim 6, wherein the extender is selected from the group consisting of marble dust, chalk, precipitated calcium carbonate, dolomite, huntite, hydromagnesite, magnesite, barium sulfate, calcium sulfate, natural phosphates, magnesium hydroxide, aluminum hydroxide, aluminum oxide, silicon dioxide in natural, ground, fumed or precipitated technical form, talcum, zeolites, kaolin, wollastonite, mica, unburnt and burnt clay minerals, perlites, glass dust, inorganic and organic fibres, and mixture thereof. 8. The method of claim 1, wherein the in-situ precipitated particles comprise calcium carbonate. 9. The method of claim 8, wherein the at least one precursor compound is a calcium compound selected from the group consisting of calcium chloride, calcium nitrate, calcium hydroxide and calcium carbonate, basic carbonate, such as sodium carbonate, and mixtures thereof. 10. The method of claim 1, wherein the in-situ precipitated particles are selected from the group consisting of calcium phosphate, aluminum phosphate, aluminum hydroxide, and mixtures thereof. 11. The method of claim 10, wherein the at least one precursor compound for the in-situ precipitation of calcium phosphate is selected from the group consisting of calcium carbonate, calcium phosphate, calcium chloride, calcium nitrate, burnt and slaked lime, as well as phosphoric acid, phosphates, hydrogenphosphate, polyphosphates, and mixtures thereof. 12. The method of claim 1, wherein the temperature of the suspension is set to values between 0° C. and 100° C. 13. The method of claim 1, wherein the composite particles are furthermore coated with one or more inorganic compounds. 14. The method of claim 13, wherein the one or more inorganic compounds is selected from the group consisting of phosphate, silicon dioxide, aluminum oxide, fluoride, or mixtures thereof. 15. The method of claim 1, wherein the composite particles are finally treated with organic additives. 16. The method of claim 1, further comprising using the composite particles in a material selected from the group consisting of coatings, plastics and laminates. 17. A method for manufacturing composite particles, containing at least one titanium dioxide particulate base component and in-situ precipitated inorganic particles comprising: providing an aqueous suspension of the particulate base component;setting the temperature of the suspension to between 0° and 100° C.;pumping the suspension through a pipeline mixer based on the rotor-stator principle;metering into the pipeline mixer at least one dissolved or dispersed precursor compound and a pH-controlling component for producing the in-situ precipitated inorganic particles;wherein no gaseous reaction component is added to the pipeline mixer;wherein the inorganic particles are predominantly precipitated in the pipeline mixer; andwherein the in-situ precipitated particles are selected from the group consisting of calcium carbonate, calcium phosphate, aluminum phosphate, aluminum hydroxide, and mixtures thereof. 18. The method of claim 17, wherein the aqueous suspension of the particulate base component is produced in an intermediate vessel equipped with a high-speed agitator having a circumferential speed of at least 15 m/s or a specific agitator capacity of at least 30 W/m3. 19. The method of claim 17, wherein in the method is operated as a continuous process. 20. The method of claim 17, wherein in the method is operated in a circuit. 21. The method of claim 17, wherein the particulate base component comprises at least one extender. 22. The method of claim 21, wherein the extender is selected from the group consisting of marble dust, chalk, precipitated calcium carbonate, dolomite, huntite, hydromagnesite, magnesite, barium sulfate, calcium sulfate, natural phosphates, magnesium hydroxide, aluminum hydroxide, aluminum oxide, silicon dioxide in natural, ground, fumed or precipitated technical form, talcum, zeolites, kaolin, wollastonite, mica, unburnt and burnt clay minerals, perlites, glass dust, inorganic and organic fibres, and mixture thereof. 23. The method of claim 17, wherein the in-situ precipitated particles comprise calcium carbonate and the at least one precursor compound is selected from the group consisting of calcium compounds, such as calcium chloride, calcium nitrate, calcium hydroxide and calcium carbonate, basic carbonate, such as sodium carbonate, and mixtures thereof. 24. The method of claim 17, wherein the in-situ precipitated particles are selected from the group consisting of calcium phosphate, aluminum phosphate, aluminum hydroxide, and mixtures thereof and the at least one precursor compound for the in-situ precipitation of calcium phosphate is selected from the group consisting of calcium carbonate, calcium phosphate, calcium chloride, calcium nitrate, burnt and slaked lime, as well as phosphoric acid, phosphates, hydrogenphosphate, polyphosphates, and mixtures thereof. 25. The method of claim 17, wherein the composite particles are furthermore coated with one or more inorganic compounds.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (5)
Brown Alan J. (Milledgeville GA) Shurling ; Jr. Dickey S. (Sandersville GA) Carswell Jenny S. (Milledgeville GA), Aggregated composite mineral pigments.
Diebold Michael P ; Bettler Charles Robert ; Niedenzu Phillip Martin ; Coombe Anhtony John ; Lanci ; Sr. John Phillip, Continuous wet treatment process to prepare durable, high gloss titanium dioxide pigment.
Guenin Eric P. ; Trotzinka Karen A. ; Smith Leslie C. ; Teffenhart John M. ; McDermott Keith J. ; Shefer Shmuel David ; Shefer Adi, Matrix composition comprising surfactant and matrix useful for targeted delivery articles.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.