A polyester film made from two kinds of polyester resins and having a specific DSC (and a specific glass transition point) is provided, (i) which is superior in mechanical property, capable of thermocompression bonding with a metal sheet, despite a high degree of crystallization of the film, reduces
A polyester film made from two kinds of polyester resins and having a specific DSC (and a specific glass transition point) is provided, (i) which is superior in mechanical property, capable of thermocompression bonding with a metal sheet, despite a high degree of crystallization of the film, reduces quality change of plastic film laminated on the metal sheet even if faced with variation of conditions of thermocompression bonding with the metal sheet, and which is capable of thermocompression bonding even at a relatively low temperature, (ii) which is superior in formability, (iii) which is superior in flavoring property and impact resistance, and which obliterates occurrence of whitening or delamination of the film, or microcracks on the film, even if the film in the metal laminated sheet obtained by thermocompression bonding of the film on the metal sheet or on the surface of a metal can obtained by subjecting the metal laminated sheet to various form processings is crystallized, and (iv) which satisfies productivity at an industrial scale.
대표청구항▼
1. A metal can or a lid of a metal can, which comprises a metal laminated sheet comprising a metal sheet and a polyester film laminated on the metal sheet, wherein the polyester film comprises a polyester resin composition comprising 30-45 wt % of a polyethylene terephthalate resin (A),55-70 wt % of
1. A metal can or a lid of a metal can, which comprises a metal laminated sheet comprising a metal sheet and a polyester film laminated on the metal sheet, wherein the polyester film comprises a polyester resin composition comprising 30-45 wt % of a polyethylene terephthalate resin (A),55-70 wt % of a polybutylene terephthalate resin (B), anda phosphorus compound of at least one kind selected from the group consisting ofbis(2,6-di-t-butyl-4-methylphenyl)pentaerythritol dibenzophosphite,bis(2,6-di-t-butyl-4-methylphenyl)pentaerythritol diphosphite,bis(2,4-dicumylphenyl)pentaerythritol diphosphite,2-[[2,4,8,10-tetrakis(1,1-dimethylether)dibenzo[d,f][1,3,2]dioxaphosphepin-6-yl]oxy]-N,N-bis[2-[2,4,8,10-tetrakis(1,1-dimethyletherdibenzo[d,f][1,3,2]dioxaphosphepin-6-yl)oxy]ethyl]ethanolamine,diphenyl isodecylphosphite,trimethyl phosphate,ethyl diethylphosphonoacetate,benzyl ethylphosphonate,tri-2-ethylhexyl phosphate,tris(2-chloroethyl)phosphate, andbis(asetodeca)pentaerythritol diphosphate, and wherein the metal catalyst for polycondensation of the polybutylene terephthalate resin (B) comprises at least one selected from tetra-n-butyl titanate and tetraisopropyl titanate,the film has a ratio [P]/[M] of the amount of phosphorus [P] (mol) in the phosphorus compound to the amount of metal [M] (mol) in a metal catalyst for polycondensation of the polyethylene terephthalate resin (A) and the polybutylene terephthalate resin (B) that is not less than 1 and not more than 81.5, andthe film after melting or softening to allow adhesion to an aluminum plate, followed by standing in a 270° C. atmosphere for 10 minutes, has 2 or more melting peaks in an area corresponding to not less than 180° C. and less than 280° C. of differential scanning calorimetry (DSC). 2. The metal can or a lid of a metal can of claim 1, wherein the polyester film has a dynamic hardness of 7.5-30 gf/μm2. 3. The metal can or a lid of a metal can of claim 1, wherein PET (A) has an intrinsic viscosity of 0.62-0.75, and PBT (B) has an intrinsic viscosity of 1.1-1.4. 4. The metal can or a lid of a metal can of claim 1, wherein the 2 or more melting peaks in an area corresponding to not less than 180° C. and less than 280° C. of DSC are a peak (TmA: 235-253° C.) derived from the polyethylene terephthalate resin (A) and a peak (TmB: 205-235° C.) derived from the polybutylene terephthalate resin (B). 5. The metal can or a lid of a metal can of claim 1, wherein the glass transition point of the polyester film is not less than 20° C. and less than 60° C.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (34)
Hasegawa Kinji (Hachioji JPX) Asai Takeo (Sagamihara JPX) Ono Mitsumasa (Sagamihara JPX) Murakami Yoji (Sagamihara JPX), Biaxially oriented laminated polyester film for use as film to be bonded onto metal sheet.
Kubo Koji,JPX ; Murooka Hirofumi,JPX ; Kosuge Masahiko,JPX ; Kimura Manabu,JPX, Biaxially oriented polyester film to be laminated onto a metal plate and molded.
Kimura Masahiro,JPX ; Takahashi Kohzo,JPX ; Kojima Hiroji,JPX ; Abe Koichi,JPX, Biaxially stretched polyester film for forming container and method of producing the film.
Hasegawa Kinji,JPX ; Asai Takeo,JPX ; Ono Mitsumasa,JPX ; Kudo Takafumi,JPX, Laminated polyester film for use as film with which metal plate is to be laminated.
Hasegawa Kinji (Hachioiji JPX) Asai Takeo (Sagamihara JPX) Murakami Yoji (Sagamihara JPX), Polyester film for lamination onto metal sheet for processing of said sheet, and use thereof.
Kosuge Masahiko,JPX ; Kimura Manabu,JPX ; Yoshida Tetsuo,JPX ; Kubo Koji,JPX ; Murooka Hirofumi,JPX ; Hasegawa Tetsuya,JPX, Polyester film for metal lamination and the use thereof.
van der Meer Roelof (Halsteren NLX) Verbraak Constantinus L. J. A. (Steenbergen NLX) Heuseveldt Jan W. (Bergen op Zoom NLX) van Helmond Johannes (Bergen op Zoom NLX) Ketels Hendrikus H. T. M. (Huyber, Polymer mixture and articles formed therefrom.
Heuseveldt Jan W. (Bergen op Zoom NLX) van Helmond Johannes (Bergen op Zoom NLX) Ketels Hendrikus H. T. M. (Huybergen NLX), Polymer mixtures and articles formed therefrom.
Russin Nicholas C. (Kingsport TN) Tershansy Ronald A. (Kingsport TN) Kibler Charles J. (Kingsport TN), Process and catalyst inhibitor systems for preparing synthetic linear polyesters.
Avramova Nadka V. (Sofia BGX) Avramov Isak A. (Sofia BGX) Fakirov Stoyko C. (Sofia DE BGX) Schultz Jerold M. (Newark DE), Process of making a blend of PET and PBT.
Yatsu Tadao (Iwakuni JPX) Todo Akira (Iwakuni JPX) Sotoyama Toshiki (Ohtake JPX), Stretched film structure of the poly-1,3-phenylene terephthalate type.
Cattron Wendell W. (Hinckley IL) Schiavone Robert J. (Geneva IL), Transesterification-inhibited polyester melt blend compositions having modified thermal properties.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.