Method for preparing support of molecular sieve membrane
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C04B-035/195
C04B-035/624
C04B-035/626
C04B-035/636
C04B-035/64
C04B-041/00
C04B-041/87
B01D-069/10
B01D-071/02
C04B-041/50
출원번호
US-0542648
(2016-07-22)
등록번호
US-10017423
(2018-07-10)
우선권정보
CN-2015 1 0991906 (2015-12-25)
국제출원번호
PCT/CN2016/091005
(2016-07-22)
국제공개번호
WO2017/107478
(2017-06-29)
발명자
/ 주소
Meng, Fanpeng
Fan, Zhenkun
Zhang, Jian
Zhang, Chao
출원인 / 주소
SHANDONG GUIYUAN ADVANCED CERAMICS CO., LTD
인용정보
피인용 횟수 :
0인용 특허 :
3
초록▼
A method for preparing a support of a molecular sieve membrane is provided and relates to a technical field of support preparation, including steps of: according to a molar ratio of magnesium, aluminum and silicon in cordierite, preparing a nanometer composite sol of magnesium, aluminum, silicon and
A method for preparing a support of a molecular sieve membrane is provided and relates to a technical field of support preparation, including steps of: according to a molar ratio of magnesium, aluminum and silicon in cordierite, preparing a nanometer composite sol of magnesium, aluminum, silicon and lanthanum serving as a sintering aid through a sol-gel method, enveloping and bonding the sol on a surface of dispersed nano-sized cordierite powders, and transforming the sol into nanometer composite oxides through presintering; mixing the cordierite powders, a binder and water, forming mud, extruding the mud, forming the mud into a green body, and sintering the green body into a cordierite support; coating a layer of film on the cordierite support with an aqueous dispersant of zirconia, then sintering, and obtaining a support of a molecular sieve membrane, composited by a cordierite main support layer and a zirconia film layer.
대표청구항▼
1. A method for preparing a support of a molecular sieve membrane, comprising steps of: (1) adding ethyl alcohol and a first weight of water into a reaction kettle, then adding cordierite powders, and uniformly stirring; adding a first dispersant, then adding tetraethoxysilane, aluminum salt, magnes
1. A method for preparing a support of a molecular sieve membrane, comprising steps of: (1) adding ethyl alcohol and a first weight of water into a reaction kettle, then adding cordierite powders, and uniformly stirring; adding a first dispersant, then adding tetraethoxysilane, aluminum salt, magnesium salt and lanthanum salt, stirring and dissolving, and obtaining a mixed liquid; increasing a temperature of the mixed liquid to 65-80° C., then adding ammonium hydroxide into the mixed liquid, and adjusting a pH value thereof to 5-6; reacting for 2-12 hours, and generating a mixed sol of silicon, aluminum, magnesium and lanthanum, wherein a proportion of silicon, aluminum and magnesium in the mixed sol is the same as that in a composition of cordierite; further adjusting the pH value to 8-9, reacting for 2-6 hours, and aging the mixed sol; pouring an obtained mixture into a container, standing and generating precipitates; washing the precipitates with reverse osmosis (RO) water, sucking and filtering liquid out, and drying the precipitates; heating the dried precipitates, keeping a temperature of the precipitates, and obtaining cordierite particles enveloped by composite nanometer oxides which are prepared according to a composition proportion of the cordierite;(2) uniformly mixing and stirring the cordierite particles, a binder, a second weight of water and a humectant, and forming mud; preparing the mud into a green body, drying the green body, and sintering the green body into a cordierite support; and(3) adding zirconia into a third weight of water, adjusting a pH value thereof to 2.5-3 with nitric acid, and uniformly stirring; then adding a second dispersant and a viscosity modifier, uniformly stirring, and obtaining a film coating solution; coating the film coating solution on an outer layer of the cordierite support, drying and sintering the cordierite support, and obtaining the cordierite support with the outer layer coated by a zirconia film layer. 2. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (1), a weight ratio of the ethyl alcohol and the water is 0.85-1.15:1; a median particle diameter D50 of the cordierite powders is 2-5 μm, and a weight of the cordierite powders is 25-35% of a total weight of the ethyl alcohol and the water; the first dispersant is a polyethylene glycol dispersant or a polyvinyl alcohol (PVA) dispersant, and a weight of the added first dispersant is 2-5% of the weight of the cordierite powders. 3. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (1), a total weight of the tetraethoxysilane, the aluminum salt, the magnesium salt and the lanthanum salt is 3-8% of a weight of the cordierite powders; and a molar ratio of silicon in the tetraethoxysilane, aluminum in the aluminum salt, magnesium in the magnesium salt and lanthanum in the lanthanum salt is 5-5.2:4:2-2.2:0-3. 4. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (1), the aluminum salt comprises at least one member selected from a group consisting of aluminum nitrate, aluminum chloride and aluminum sulfate; the magnesium salt comprises at least one member selected from a group consisting of magnesium nitrate, magnesium chloride and magnesium sulfate; and the lanthanum salt comprises at least one member selected from a group consisting of lanthanum nitrate, lanthanum chloride and lanthanum sulfate. 5. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (1), a heating temperature is 450-650° C. and kept for 1-6 hours. 6. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (2), the binder is methylcellulose or hydroxypropyl methyl cellulose, and a weight of the added binder is 4-10% of a weight of the cordierite particles; the second weight of the water is 20-40% of the weight of the cordierite particles; the humectant is glycerinum, and a weight of the added humectant is 1.5-3.5% of the weight of the cordierite particles. 7. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (2), the green body is a circular tubular green body having a single hole, three holes or four holes. 8. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (2), a sintering temperature is 950-1150° C. and a sintering time is 1-6 hours. 9. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (3), a median particle diameter D50 of the zirconia is 0.25-0.6 μm, and a weight of the added zirconia is 10-20% of the third weight of water in the film coating solution; the second dispersant is a polyethylene glycol dispersant, and a weight of the added second dispersant is 2-5% of the weight of the zirconia; the viscosity modifier is hydroxypropyl methyl cellulose, and a weight of the added viscosity modifier is 0.65-1.5% of the third weight of water in the film coating solution; and a weight of the film coating solution is 6-12% of a weight of the cordierite support. 10. The method for preparing the support of the molecular sieve membrane, as recited in claim 1, wherein: in the step (3), a sintering temperature is 950-1150° C. and a sintering time is 2-4 hours.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (3)
Okada Jun (Yokohama JPX) Okada Akihide (Yokohama JPX), Catalysts for emission control of aldehyde.
Barringer Eric A. (Waltham MA) Lieberman Sheldon I. (Burlington MA) Schmidt Mark S. (West Newton MA) Hodge James D. (Medway MA), Method for producing materials for co-sintering.
Dalla Betta Ralph A. (Mountain View CA) Tsurumi Kazunori (Fujisawa CA JPX) Shoji Toru (Sunnyvale CA) Garten Robert L. (Cupertino CA), Partial combustion catalyst of palladium on a zirconia support and a process for using it.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.