Dental glass-ionomer cement composition and method of preparing the same
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C08K-003/40
C09D-135/00
A61K-006/00
A61K-006/083
출원번호
US-0941606
(2015-11-15)
등록번호
US-10023721
(2018-07-17)
우선권정보
KR-10-2014-0167565 (2014-11-27)
발명자
/ 주소
Lee, Na Ri
Kim, Ki Hoon
Kim, Jae Hwan
Lee, Do Weon
Kim, Min-Sung
출원인 / 주소
SPIDENT CO., LTD.
대리인 / 주소
The PL Law Group, PLLC
인용정보
피인용 횟수 :
0인용 특허 :
10
초록▼
Disclosed is a dental glass-ionomer cement composition, which includes polycarboxylic acid, water, and a glass powder including a metal component that is able to form an ionic bond with a carboxyl group of polycarboxylic acid in the presence of water and having a polymer material that is applied on
Disclosed is a dental glass-ionomer cement composition, which includes polycarboxylic acid, water, and a glass powder including a metal component that is able to form an ionic bond with a carboxyl group of polycarboxylic acid in the presence of water and having a polymer material that is applied on at least a portion of the surface of the glass powder. The dental glass-ionomer cement composition can guarantee sufficient working time and can exhibit increased initial strength.
대표청구항▼
1. A dental glass-ionomer cement composition, comprising: polycarboxylic acid;water; anda glass powder comprising a metal component that is able to form an ionic bond with a carboxyl group of the polycarboxylic acid in presence of water, wherein at least a portion of a surface of the glass powder ha
1. A dental glass-ionomer cement composition, comprising: polycarboxylic acid;water; anda glass powder comprising a metal component that is able to form an ionic bond with a carboxyl group of the polycarboxylic acid in presence of water, wherein at least a portion of a surface of the glass powder have been coated with a polymer, wherein the polymer is obtained by polymerizing a monomer having a carboxylic acid group, and the polymer is included in an amount of 6 parts by weight based on 100 parts by weight of the glass powder. 2. The dental glass-ionomer cement composition of claim 1, wherein the polycarboxylic acid has at least one of repeating units represented by Chemical Formulas 1 to 3 below: wherein R1 and R2 are identical to or different from each other, and are each independently any one selected from among hydrogen, a substituted or unsubstituted C1-C20 alkyl group, a substituted or unsubstituted C6-C18 aryl group, a substituted or unsubstituted C7-C30 aralkyl group, and a silyl group having substituted or unsubstituted C1-C30 alkyl or C6-C24 aryl; andR is any one selected from among a substituted or unsubstituted C1-C20 alkylene group, a substituted or unsubstituted C6-C18 arylene group, and a substituted or unsubstituted C7-C30 aralkylene group. 3. The dental glass-ionomer cement composition of claim 1, wherein the polycarboxylic acid is obtained by polymerizing or copolymerizing any one or a mixture of two or more selected from among acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid, and itaconic acid. 4. The dental glass-ionomer cement composition of claim 1, wherein the metal component of the glass powder, which is able to form an ionic bond with the carboxyl group of the polycarboxylic acid, comprises any one or more selected from among an alkali metal, an alkaline earth metal, a transition metal, and aluminum. 5. The dental glass-ionomer cement composition of claim 1, wherein the polymer material, which is applied on the glass powder, has a larger number average molecular weight than a number average molecular weight of the polycarboxylic acid. 6. The dental glass-ionomer cement composition of claim 1, further comprising a fluorine component. 7. The dental glass-ionomer cement composition of claim 1, wherein the dental glass-ionomer cement composition comprises, based on 100 parts by weight of the polycarboxylic acid, 20 to 500 parts by weight of water and 25 to 1000 parts by weight of the glass powder. 8. The dental glass-ionomer cement composition of claim 1, further comprising: a polymerizable monomer; anda chemical polymerization catalyst or photopolymerization catalyst,wherein the polymerizable monomer is polymerized using the catalyst. 9. The dental glass-ionomer cement composition of claim 1, wherein said at least the portion of the surface of the glass powder coated with the polymer material is produced by a process selected from the group consisting of mixing the glass powder with a solution of the polymer material and removing a solvent of the solution, immersing the glass powder in the solution of the polymer material and taking the glass powder out of the solution, and spraying the solution of the polymer material onto the glass powder. 10. The dental glass-ionomer cement composition of claim 1, wherein the polymer material is formed by polymerizing a monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid, itaconic acid, 2-chloroacrylic acid, 3-chloroacrylic acid, 2-bromoacrylic acid, and 3-bromoacrylic acid. 11. A dental glass-ionomer cement composition produced by a process comprising: coating at least a portion of a surface of a glass powder with a polymer material; andafter the coating, mixing the glass powder coated with the polymer material with polycarboxylic acid in the presence of water,wherein the polymer material is obtained by polymerizing a monomer having a carboxylic acid group, and the polymer material is included in an amount of 6 parts by weight based on 100 parts by weight of the glass powder. 12. The dental glass-ionomer cement composition of claim 11, wherein the process further comprises, after the coating, polymerizing a monomer by using a chemical polymerization catalyst or a photopolymerization catalyst. 13. The dental glass-ionomer cement composition of claim 11, wherein the coating comprises a process selected from the group consisting of (i) mixing the glass powder with a solution of the polymer material and removing a solvent of the solution, (ii) immersing the glass powder in the solution of the polymer material and taking the glass powder out of the solution, and (iii) spraying the solution of the polymer material onto the glass powder. 14. The dental glass-ionomer cement composition of claim 11, wherein the polymer material is formed by polymerizing a monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic acid, maleic anhydride, fumaric acid, itaconic acid, 2-chloroacrylic acid, 3-chloroacrylic acid, 2-bromoacrylic acid, and 3-bromoacrylic acid.