초록 ▼

Polypyrrole/carbon (PPy/C) composite doped with organic anion p-toluenesulfonate (pTS) is utilized as an electrode in supercapacitor for energy storage application. The surface initiated in-situ chemical oxidative polymerization yields a composite material PPy/C in the presence of varying concentrat

Polypyrrole/carbon (PPy/C) composite doped with organic anion p-toluenesulfonate (pTS) is utilized as an electrode in supercapacitor for energy storage application. The surface initiated in-situ chemical oxidative polymerization yields a composite material PPy/C in the presence of varying concentrations of pTS. The novelty of the present invention lies in the doping of PPy/C composite with organic anion pTS and consequent enhancement of its electrochemical activity and stability. The conjugation length and electrical conductivity of pTS doped PPy/C composites increase with the increase in dopant concentration. The pTS doped PPy/C composite synthesized using equimolar concentration (0.1 M) of pTS to pyrrole shows the maximum specific capacitance of ˜395 F/g in 0.5 M Na2SO4 aqueous solution with significant stability ˜95% capacitance retention after ˜500 cycles.

대표청구항 ▼

1. A process for preparing a p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite comprising the steps of: i) treating carbon black with 6 M HNO3 for 2-4 h;ii) ultrasonic dispersion of treated carbon black as obtained in step (i) in water for 50 to 70 min to form

1. A process for preparing a p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite comprising the steps of: i) treating carbon black with 6 M HNO3 for 2-4 h;ii) ultrasonic dispersion of treated carbon black as obtained in step (i) in water for 50 to 70 min to form a uniform suspension;iii) adding 0.1 M distilled pyrrole monomer to the suspension as obtained in step (ii) followed by adding 0.06-0.1 M pTS at temperature in the range of 273-280 K to obtain a solution;iv) constantly stirring the solution of step (iii) under inert atmosphere for 30-45 min at 273-280 K to obtain a stirred solution;v) adding 10-30 ml of ammonium persulfate (APS) solution comprising a molar ratio of ammonium persulfate to pyrrole of 1:1 dropwise to the stirred solution of (iv) with constant stirring for period in the range of 8-12 h to obtain a precipitate;vi) filtering and washing of the precipitate obtained from (v) and keeping it in an oven at 313-353 K for 10-14 h to obtain a p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite. 2. The process for preparing a p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite according to claim 1, wherein the washing of the precipitate obtained from (v) comprises washing with methanol and water. 3. The process for preparing a p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite according to claim 1, wherein the inert atmosphere comprises a gas selected from the group consisting of nitrogen, argon and helium. 4. A process for preparing an electrode for a supercapacitor comprising the steps of: i) treating carbon black with 6 M HNO3 for 2-4 h;ii) ultrasonic dispersion of treated carbon black as obtained in step (i) in water for 50 to 70 min to form a uniform suspension;iii) adding 0.1 M distilled pyrrole monomer to the suspension as obtained in step (ii) followed by adding 0.06-0.1 M pTS at temperature in the range of 273-280 K to obtain a solution;iv) constantly stirring the solution of step (iii) under inert atmosphere for 30-45 min at 273-280 K to obtain a stirred solution;v) adding 10-30 ml of ammonium persulfate (APS) solution comprising a molar ratio of ammonium persulfate to pyrrole of 1:1 dropwise to the stirred solution of (iv) with constant stirring for period in the range of 8-12 h to obtain a precipitate;vi) filtering and washing of the precipitate obtained from (v) and keeping it in an oven at 313-353 K for 10-14 h to obtain a p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite,a) adding 80-90 wt. % of the p-toluenesulfonate (pTS) doped conducting polypyrrole/acid-treated carbon black composite and 10-20 wt. % of a polyvinylidene fluoride (PVDF) in N,N-dimethylformamide (DMF) followed by ultrasonicating for 50 to 60 min to form a uniform slurry;b) coating a platinum (Pt) disk working electrode with the slurry obtained in step a to cover only a top active surface of the electrode;c) drying the electrode in an oven at 313-353 K for 30-45 min to obtain the electrode. 5. The process for preparing an electrode according to claim 4, wherein specific capacitance of the electrode is 395 F/g in 0.5 M Na2SO4 aqueous solution with 95% capacitance retention after 500 cycles.