초록 ▼

Layered structures consisting of at least one film A containing a polyvinyl acetal PA and at most 16% by weight of plasticizer WA and at least one film B containing a polyvinyl acetal PB and at least 16% by weight plasticizer WB between two glass sheets, are produced by adhering at least one film A

Layered structures consisting of at least one film A containing a polyvinyl acetal PA and at most 16% by weight of plasticizer WA and at least one film B containing a polyvinyl acetal PB and at least 16% by weight plasticizer WB between two glass sheets, are produced by adhering at least one film A to at least one film B or at least one of the glass sheets by means of a liquid. The layered structure can then be pressed to form a composite glass laminate.

대표청구항 ▼

1. A method for producing a layered structure comprising at least one film A containing a polyvinyl acetal PA and at most 16% by weight of plasticiser WA and at least one film B containing a polyvinyl acetal PB and at least 16% by weight plasticiser WB and two glass sheets, comprising applying an or

1. A method for producing a layered structure comprising at least one film A containing a polyvinyl acetal PA and at most 16% by weight of plasticiser WA and at least one film B containing a polyvinyl acetal PB and at least 16% by weight plasticiser WB and two glass sheets, comprising applying an organic liquid having a boiling point of more than 120° C. to at least one film A and/or to at least one film B to wet the film or films, adhering films A and B to each other by means of the liquid, and then contacting the adhering films A and B with the glass sheets to form a laminatable composite, and laminating the composite to form the layered structure. 2. The method of claim 1, wherein the liquid comprises plasticiser WA and/or plasticiser WB. 3. The method of claim 1, wherein film A and/or a glass surface is/are wetted with the liquid by spraying, painting, placement of drops or printing. 4. The method of claim 1, wherein the film A comprises a polyvinyl acetal PA with a proportion of vinyl alcohol groups of from 6 to 26% by weight and the film B comprises a polyvinyl acetal PB with a proportion of vinyl alcohol groups of from 14 to 26% by weight. 5. The method of claim 1, wherein film A has a smaller surface area than film B such that film B extends beyond film A when films A and B are joined together. 6. The method of claim 1, wherein film A has electrically conductive structures. 7. The method of claim 6, wherein the film A is printed. 8. The method of claim 1, wherein film A is at least partly non-transparent and/or coloured and/or opaque. 9. The method of claim 1, wherein film A at least a portion thereof has heat radiation-shielding layers or nanoparticles. 10. The method of claim 1, wherein the film B is acoustically damping. 11. The method of claim 1, wherein film B has a coloured area. 12. The method of claim 1, wherein film B has a wedge-shaped thickness profile. 13. The method of claim 1, wherein film A contains 0 to 8 wt. % of plasticizer WA prior to applying the liquid. 14. The method of claim 1, wherein following forming an assembly of said two glass panes and films A and B, the assembly is laminated in an autoclave. 15. The method of claim 1, wherein a thickness of film A prior to laminating is 20% or less of a thickness of film B prior to laminating. 16. A method for producing a layered structure comprising at least one film A containing a polyvinyl acetal PA and at most 16% by weight of plasticizer WA and at least one film B containing a polyvinyl acetal PB and at least 16% by weight plasticizer WB between two glass sheets, comprising adhering at least one film A to at least one film B by means of an organic liquid having a boiling point of more than 120° C., wherein film A has at least one opening, such that by means of this opening the film B is in direct contact with the glass sheet bearing against film A. 17. An autoclave process for preparing a laminated safety glass comprising two glass panes and a multilayer laminating film comprising at least film A comprising polyvinyl acetal PA and 0-16 wt. % of plasticizer WA, and at least one film B comprising polyvinyl acetal PB and 16 wt. % or more of plasticizer WB, the content of plasticizer WB in film B being greater than the content of plasticizer WA in film A on a weight percentage basis, comprising wetting a surface of film A which will contact film B and/or wetting a surface of film B which will contact film A with an organic liquid having a boiling point of more than 120° C., adhering films A and B together by means of the organic liquid to form a multilayer film, positioning the multilayer film between two glass panes, and autoclaving a composite thus produced in an autoclave to form a laminated glass. 18. The process of claim 17, wherein film A has a content of plasticizer WA of from 0% to 8% prior to laminating. 19. The process of claim 17, wherein a thickness of film A prior to laminating is 20% or less of a thickness of film B prior to laminating.