Thermal insulation material and method for making the same
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C04B-038/10
C04B-038/02
C04B-028/06
C04B-028/16
C04B-111/28
출원번호
US-0522279
(2011-01-13)
등록번호
US-10160691
(2018-12-25)
우선권정보
FR-10 50212 (2010-01-13)
국제출원번호
PCT/FR2011/050066
(2011-01-13)
§371/§102 date
20120713
(20120713)
국제공개번호
WO2011/086333
(2011-07-21)
발명자
/ 주소
Prat, Evelyne
Frouin, Laurent
Taquet, Pascal
Mahiaoui, Jamel
출원인 / 주소
KERNEOS
대리인 / 주소
Young & Thompson
인용정보
피인용 횟수 :
0인용 특허 :
10
초록▼
A cellular structure thermal insulation material includes by weight as compared to the material total weight: from 4 to 96% of a hydraulic binder, which prior to being contacted with water, includes at least one phase selected from C3A, CA, C12A7, C11A7CaF2, C4A3$ (Yee lemite), C2A(1-x)Fx (where x b
A cellular structure thermal insulation material includes by weight as compared to the material total weight: from 4 to 96% of a hydraulic binder, which prior to being contacted with water, includes at least one phase selected from C3A, CA, C12A7, C11A7CaF2, C4A3$ (Yee lemite), C2A(1-x)Fx (where x belongs to 0, 1), hydraulic amorphous phases having a C/A molar ratio ranging from 0.3 to 15 and such that cumulated amounts of Al2O3 of these phases be ranging from 3 to 70% by weight of the hydraulic binder total weight,from 4 to 96% of at least one filler,the material having a pore volume ranging from 70% to 95%. The use of a mineral foam for making thermal insulation material as well as methods for making the mineral foam are also described.
대표청구항▼
1. A cellular structure thermal insulation material, comprising a) from 20% to 60% by weight of the insulation material of a cement matrix, the cement matrix obtained by hydration of a hydraulic binder that comprises from 10% to 50% of calcium sulfate as compared to the hydraulic binder total weight
1. A cellular structure thermal insulation material, comprising a) from 20% to 60% by weight of the insulation material of a cement matrix, the cement matrix obtained by hydration of a hydraulic binder that comprises from 10% to 50% of calcium sulfate as compared to the hydraulic binder total weight, and that prior to being contacted with water, comprises at least one phase selected from C3A, CA, C12A7, C11A7CaF2, C4A3$ (Ye'elimite), C2A(1-x)Fx (where x belongs to [0, 1]), and hydraulic amorphous phases having a C/A molar ratio ranging from 0.3 to 15, wherein the cumulative amount of Al2O3 of said at least one phase ranges from 3% to 70% by weight of the hydraulic binder total weight; andb) from 4% to 80% by weight of the insulation material of at least one filler, the at least one filler selected from the group consisting of reactive filler, inert filler, hollow filler, and a mixture thereof,said thermal insulation material having a pore volume ranging from 70% to 95% of the total volume, a density lower than or equal to 300 kg/m3, a coefficient of thermal conductivity at 20° C. lower than or equal to 0.2 W/m° C., and presents a cell mean size of less than 500 μm. 2. The cellular structure thermal insulation material according to claim 1, which presents a shrinkage lower than 500 μm/m. 3. The cellular structure thermal insulation material according to claim 1, comprising from 1% to 80% by weight of low density hollow fillers. 4. The mineral foam according to claim 1, which further comprises at least one compound selected from foaming agents, air-entraining agents and gas-generating agents. 5. The cellular structure thermal insulation material according to claim 1, which presents a compressive strength Cs at 3 hours higher than or equal to 0.2 MPa. 6. The cellular structure thermal insulation material according to claim 1, which presents a compressive strength Cs value higher than 0.3 MPa, and a coefficient of thermal conductivity at 20° C. lower than or equal to 0.08 W/m° C. 7. The cellular structure thermal insulation material according to claim 1, which presents after 24 hours a compressive strength Cs value higher than 0.8 MPa, and a coefficient of thermal conductivity at 20° C. ranging from 0.08 to 0.2 W/m° C. 8. The cellular structure thermal insulation material according to claim 1, which presents after 24 hours a compressive strength Cs value higher than 1.5 MPa, and a coefficient of thermal conductivity at 20° C. ranging from 0.08 to 0.2 W/m° C. 9. The cellular structure thermal insulation material according to claim 1, wherein the binder of the insulating material further comprises from 0% to less than 5% by weight, as related to the hydraulic binder total weight, of Portland cement. 10. The cellular structure thermal insulation material according to claim 1, wherein the weight ratio of water to hydraulic binder is in a range of from 0.1 to 0.7. 11. The cellular structure thermal insulation material according to claim 1, wherein the weight ratio of water to hydraulic binder is in a range of from 0.15 to 0.5. 12. The cellular structure thermal insulation material according to claim 1, which presents a cell mean size of less than 300 μm. 13. The cellular structure thermal insulation material according to claim 1, wherein the hydraulic binder comprises from 20% to 40% by weight of calcium sulfate. 14. The cellular structure thermal insulation material according to claim 1, wherein the at least one filler is selected from the group consisting of silica fume, blast furnace slag, steel slag, fly ash, limestone fillers, particulate silica, silicas including pyrogenated and precipitated silicas, silicas recovered in rice husks, diatomaceous silicas, calcium carbonates, calcium silicates, barium sulfate, metakaolins, titanium, iron, zinc, chromium, zirconia, magnesium metal oxides, alumina under its various forms (hydrated or not), alumina hollow beads, boron nitride, lithopone, barium metaborate, calcinated, standard or expanded clays, perlite, vermiculite, pumices, rhyolite, chamotte, talc, mica, optionally hollow, glass beads or expanded glass granules, silicate foam grains, silica aerogels, sands, broken gravels, gravels, pebbles, carbonate black, silicon carbide, corundum, rubber granules, wood and straw. 15. The cellular structure thermal insulation material according to claim 1, having a density ranging from 80 kg/m3 to 250 kg/m3. 16. The cellular structure thermal insulation material according to claim 1, wherein the cumulative amount of Al2O3 of said at least one phase ranges from 20% to 30% by weight of the hydraulic binder total weight.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (10)
Dean L. Putt ; Marsha Stalker Bischel ; Anthony L. Wiker ; Andrea M. Moser, Durable porous article of manufacture and a process to create same.
Plunguian Mark (6912 Columbia Drive BOTH OF ; Alexandria VA 22307) Cornwell Charles E. (7104 Marlan Drive BOTH OF ; Alexandria VA 22307), Foamed cementitious compositions and method of producing same.
Chao Yen-Yau H. (Harleysville PA) Larson Gary R. (Hatfield PA) Linder Linus W. (Lansdale PA) Bauman Mike J. (Mundelein IL), Foamed hydraulic compositions containing copolymeric foam stabilizers.