The present invention relates to interior and exterior materials for an automobile, comprising: a polyester resin foam layer; and a fiber layer laminated on one side or both sides of the polyester resin foam layer. The interior and exterior materials for an automobile can enhance durability and stre
The present invention relates to interior and exterior materials for an automobile, comprising: a polyester resin foam layer; and a fiber layer laminated on one side or both sides of the polyester resin foam layer. The interior and exterior materials for an automobile can enhance durability and strength, reduce weight, and improve a work environment.
대표청구항▼
1. A vehicle interior or exterior material, comprising: a polyester resin foam layer having a mass per unit area in a range of 750 to 1,000 g/m2;a polyester fiber layer, formed on one surface or both surfaces of the polyester resin foam layer;a biaxially-oriented polyester film formed between the po
1. A vehicle interior or exterior material, comprising: a polyester resin foam layer having a mass per unit area in a range of 750 to 1,000 g/m2;a polyester fiber layer, formed on one surface or both surfaces of the polyester resin foam layer;a biaxially-oriented polyester film formed between the polyester resin foam layer and the polyester fiber layer;a first polyester resin adhesive layer formed between the polyester resin foam layer and the biaxially-oriented polyester film; anda second polyester resin adhesive layer formed between the biaxially-oriented polyester film and the polyester fiber layer,wherein the polyester resin foam layer is a polyethylene terephthalate (PET) resin foam layer, the polyester fiber layer includes a polyethylene terephthalate fiber layer, and each of the first and second polyester resin adhesive layers is a condensation-polymerization product of a soft segment, which is a polyol, and a hard segment, which is an esterification reaction product of a diol and a dicarbonic acid,wherein the interior or exterior material has a mass per unit area in a range of 800 to 1,100 g/m2,wherein the number of cells of the polyester resin foam layer is 1 to 30 cells per 1 mm2,wherein a variation in cell size of the polyester resin foam layer is 5% or less,wherein the polyester resin foam layer has a flexural strength of 10 N or more which is measured when a specimen is fixed with a 100 mm support span and a flexural load is applied thereto at a rate of 5 mm/min according to ASTM D 790,wherein the vehicle interior or exterior material has a noise absorption rate of 0.4 NRC or more which is measured according to KS F 2805, and a sound transmission loss value of 10 dB or more which is measured according to KS F 2080,wherein the vehicle interior or exterior material satisfies the following Expression 1 after a severe condition including a step of leaving the vehicle interior or exterior material at a temperature of 90±1° C. for 24 hours and a step of leaving the vehicle interior or exterior material at a temperature of 50±1° C. and a relative humidity of 90% for 24 hours: |V1−V0|/V0×100≤5% [Expression 1]wherein V0 is a volume (mm3) of the vehicle interior or exterior material before exposure to the severe condition, and V1 is a volume (mm3) of the vehicle interior or exterior material after exposure to the severe condition;wherein the vehicle interior or exterior material has a color difference change rate of less than 3% and a grayscale change rate of less than 3% before and after irradiation of light having a wavelength of 300 to 400 nm at an irradiation dose of 126 MJ according to an accelerated light resistance test of KS R 0021,wherein the polyester fiber layer is formed of an aggregate of modified cross section hollow fibers, the modified cross section hollow fiber includes a hollow part, a shape maintaining part and a volume control part on the basis of a cross-sectional shape, and the volume control part has a shape which protrudes in a direction opposite to a center of a fiber in which an end part has a round shape. 2. The vehicle interior or exterior material according to claim 1, wherein 90% or more of cells are closed cells (DIN ISO 4590) in the polyester resin foam layer. 3. The vehicle interior or exterior material according to claim 1, wherein the polyester resin foam layer has an average thickness in a range of 1 to 30 mm, and the fiber layer has an average thickness in a range of 0.1 to 10 mm. 4. The vehicle interior or exterior material according to claim 1, wherein the vehicle interior or exterior material is comprised in one or more of a head liner, a flow under cover, an engine room cover, a trunk room panel, a package tray, a seatback and a bumper. 5. The vehicle interior or exterior material according to claim 4, wherein the head liner has a flexural modulus of 400 to 3,000 MPa which is measured when a specimen is fixed with a 100 mm support span and a flexural load is applied thereto at a rate of 5 mm/min according to ASTM D 790.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.