Calcium silicate powders are provided. The calcium silicate powders comprise porous calcium silicate particles and an additive, the additive being at least partially penetrated into the pores of the particles. The additive is present in an amount of between 1.5 and 50%w, wherein %w is the weight rat
Calcium silicate powders are provided. The calcium silicate powders comprise porous calcium silicate particles and an additive, the additive being at least partially penetrated into the pores of the particles. The additive is present in an amount of between 1.5 and 50%w, wherein %w is the weight ratio, expressed as percentage, of the dry weight of the additive over the dry weight of the combination of the calcium silicate particles and additive.
대표청구항▼
1. A calcium silicate powder comprising discrete porous calcium silicate particles having a specific surface area with a BET value of 30 to 60 m2/g and a pore size of at least 0.01 microns and no greater than 5 microns, andseparate particles of an additive,said additive being at least partially pene
1. A calcium silicate powder comprising discrete porous calcium silicate particles having a specific surface area with a BET value of 30 to 60 m2/g and a pore size of at least 0.01 microns and no greater than 5 microns, andseparate particles of an additive,said additive being at least partially penetrating into the pores of said calcium silicate particles,the additive is present in an amount of between 1.5 and 50%w, wherein %w is the weight ratio, expressed as percentage, of the dry weight of the additive over the dry weight of the combination of said calcium silicate particles and additive, andthe additive is an alkali silicate or a combination of alkali silicates. 2. A calcium silicate powder according to claim 1, wherein at least 25%w of the additive is penetrated into the pores of the particles. 3. A calcium silicate powder according to claim 2, wherein more than or equal to 50%w of the additive is penetrated into the pores of the particles. 4. A calcium silicate powder according to claim 2, wherein more than or equal to 75%w is penetrated into the pores of the particles. 5. A calcium silicate powder according to claim 1, said calcium silicate particles comprise synthetic porous calcium silicate particles. 6. A calcium silicate powder according to claim 1, said calcium silicate particles comprise synthetic porous calcium silicate, wherein said porous calcium silicate particles are porous calcium silicate hydrate particles. 7. A calcium silicate powder according to claim 6, wherein said porous calcium silicate particles comprise xonotlite and/or tobermorite crystals. 8. A calcium silicate powder according to claim 7, wherein the weight ratio xonotlite/tobermorite is in the range of 95/5 to 5/95, inclusive. 9. A calcium silicate powder according to claim 5, wherein the porous calcium silicate particles comprise crystalline material in an amount in the range of 60 to 95%w, this %w being based upon the total weight of the particles. 10. A calcium silicate powder according to claim 1, wherein the porous calcium silicate particles have pores providing at least 75% of the particle volume. 11. A calcium silicate powder according to claim 1, wherein said additive is sodium silicate. 12. A calcium silicate powder according to claim 11, wherein the additive is sodium silicate with a SiO2:Na2O ratio of no more than 3.5. 13. A calcium silicate powder according to claim 11, wherein the additive is sodium silicate with a SiO2:Na2O ratio of at least 1.60. 14. A calcium silicate powder according to claim 11, wherein the SiO2:Na2O ratio is at least 3.00. 15. A friction brake comprising the calcium silicate powder according to claim 1. 16. A calcium silicate powder according to claim 1, consisting of said porous calcium silicate particles and said alkali silicate or combination of alkali silicates at least partially penetrating into the pores of the calcium silicate particles. 17. A calcium silicate powder according to claim 1, wherein the discrete porous calcium silicate particles have a specific surface area with a BET value of 30 to 50 m2/g. 18. A calcium silicate powder according to claim 1, wherein the additive is present in an amount of between 13 and 45%w. 19. A calcium silicate powder according to claim 18, wherein the additive is present in an amount of between 20 and 40%w. 20. A calcium silicate powder according to claim 1, wherein the calcium silicate particles have a pore size of at least 0.1 microns and no greater than 5 microns. 21. A calcium silicate powder according to claim 12, wherein the SiO2:Na2O ratio is no more than 3.25. 22. A calcium silicate powder according to claim 13, wherein the SiO2:Na2O ratio is at least 3.00. 23. A calcium silicate powder according to claim 12, wherein the SiO2:Na2O ratio is at least 1.60. 24. A calcium silicate powder according to claim 14, wherein the SiO2:Na2O ratio is no more than 3.25. 25. A calcium silicate powder according to claim 1, wherein the additive is in the form of waterglass when combined with the discrete calcium silicate particles.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.