초록

가.기술정보 및 국내외 실태조사.
나.비정질 제조설비 System설계 및 제작기술 개발.
다.전기기기용 저손실 자심재료 개발

Abstract ▼

Rapid Solidification of certain alloys from the melt results in glassy materials at ribbon or sheet form. Non-crystalline soft magnetic materials intended for use in various frequency (50$\sim$ above 100KHz) applications are shown to outperform existing crystalline materials.
We used p

Rapid Solidification of certain alloys from the melt results in glassy materials at ribbon or sheet form. Non-crystalline soft magnetic materials intended for use in various frequency (50$\sim$ above 100KHz) applications are shown to outperform existing crystalline materials.
We used plannar flow casting(PFC) method adapting for mass production system to prepare ribbon alloys data, compared PFC theoretical formula with experimental.

목차 Contents

• CHAPTER 1. 서 론...11
• 1.1 리본제조...11
• 1.1.1 열전달...11
• 1.1.1.1 열전달의 종류...11
• 1.1.1.2 전도...11
• 1.1.1.3 대류...12
• 1.1.1.4 리본제조시 열전달...13
• 1.1.2 리본-Wheel접착 동력학...17
• 1.1.3 리본 형상에 있어서 주요 제조변수의 영향...23
• 1.2 고주파용 자성 재료...30
• 1.2.1 Nonocrystalline 연자성 재료...31
• 1.2.2 비정질 자성합금의 물성과 고주파 자기특성...34
• 1.3 고주파용 비정질 합금의 응용...48
• 1.3.1 고주파 Trans에의 응용...48
• 1.3.2 SWR에의 응용...53
• CHAPTER 2. 실험방법...58
• 2.1 비정질 시편의 제작...58
• 2.1.1 모합금의 제작...58
• 2.1.2 비정질 합금 리본의 제작...59
• 2.2 X선회절 및 DTA실험...59
• 2.3 열처리...60
• 2.4 자기특성 측정...60
• 2.4.1 B-H특성...60
• 2.4.2 Coreloss측정...60
• 2.4.3 초투자율 측정...62
• CHAPTER 3. 결과 및 고찰...63
• 3.1 비정질 합금의 리본 제조...63
• 3.1.1 Wheel...63
• 3.1.2 Nozzle...64
• 3.1.3 기타설비...66
• 3.1.4 결과 및 고찰...68
• 3.2 휠 냉각계통의 설계...70
• 3.2.1 열전달...72
• 3.2.2 냉각계통의 설계사양...76
• 3.3 자기특성...79
• 3.3.1 결정화...79
• 3.3.2 자기특성...80
• CHAPTER 4. 결 론...95
• 참고문헌...96