초록

본 연구에서는 분무성형법과 잉곳트 주조법로 고 Si 규소강 시편을 제조하였다. 잉곳트 주조로는 strip casting 효과를 모사하기 위하여 10㎜ 두께의 잉곳트를 제조하여 실험하였다. 주조방법(잉곳트 주조법, 분무성형법), 열처리 조건(균질화 열처리, 규칙상 제거를 위한 소둔), Si 함량 그리고 조업 온도가 편석 특성, 규칙상의 생성 및 제거 그리고 냉간 가공성에 미치는 영향을 조사하였다. 실험에 쓰인 Si 조성은 5∼6.5% 였다.

Abstract ▼

In this study the high Si steel specimen was made by spray forming and ingot casting. 10㎜ thickness ingot was cast to simulate the effect of strip casting. The effect of casting methods (ingot casting and spray casting), heat treatment conditions (homogenization and annealing to remove ordered phase

In this study the high Si steel specimen was made by spray forming and ingot casting. 10㎜ thickness ingot was cast to simulate the effect of strip casting. The effect of casting methods (ingot casting and spray casting), heat treatment conditions (homogenization and annealing to remove ordered phases), Si content and working temperature on segregation characteristics, the formation or the disappearance of ordered phases and cold-workability were investigated. The Si-content between 5 and 6.5% was used in experiment.

목차 Contents

• 제 1 장. 서론...13
• 제 2 장. 국내외 기술개발 현황...15
• 제 3 장. 연구개발수행 내용 및 결과...19
• 제 1 절. 제조공정...19
• 제 2 절. 주조 방법에 따른 조직 및 편석 특성...22
• 1. 실험방법...22
• 2. 실험결과 및 고찰...24
• 가. 분무 조건이 분무성형체에 미치는 영향...24
• 나. 주조방법에 따른 편석 특성...27
• 3. 결론...33
• 제 3 절. 규칙상의 특성...34
• 1. 실험방법...34
• 2. 실험결과 및 고찰...38
• 가. 주조방법과 열처리 조건의 영향...38
• 나. Si 함량의 영향...42
• 다. 제 3 합금원소의 영향...45
• 라. 소둔 온도 및 시간의 영향...48
• 마. 균질화 과정에 따른 전기비저항 변화...55
• 3. 결론...57
• 제 4 절. 기계적 성질...58
• 1. 실험방법...58
• 2. 결과 및 고찰...60
• 가. 열간압연 및 ？？칭 특성...60
• 나. 주조방법 및 열처리 조건이 냉간 가공성에 미치는 영향...62
• (1) 냉간압연 및 경도실험 결과...62
• (2) 인장실험 결과...67
• (3) 규칙상 및 미세조직 조사...69
• (4) 고찰...70
• 다. 냉간 가공성에 미치는 온도의 영향...75
• (1) 200℃ 온간 압연 결과...75
• (2) 150℃에서의 인장실험 결과...76
• (3) 온도가 유동성질에 미치는 효과...79
• 3. 결론...89
• 제 5 절. 전기자기적 성질...91
• 제 4 장. 연구개발목표 달성도 및 대외기여도...92
• 제 1 절. 연구개발목표 달성도...92
• 제 2 절. 대외 기여도...93
• 제 5 장. 연구개발결과의 활용계획...94
• 제 6 장. 참고문헌...95