초록

-용접변수에 따른 압력용기 클래드 재의 미세조직 관찰 (OEM,SEM,TEM)
-중성자 조사 후의 조사유기 손상 관찰 (TEM)
-조사전후 소형인장 시험
-소형펀치 시험장치 및 저온유지장치 제작
-중성자 조사전의 상온 및 저온에서 SP 시험 수행
-클래드 재에 따른 천이온도 특성 분석
-인장특성과 SP시험간의 연관성 조사 분석
-중성자 조사후의 SP 특성치 평가
-파면관찰

Abstract ▼

To use the small specimen techniques for evaluating the microstructural and mechanical property changes on nuclear reactor pressure vessel cald with neutron irradiation, the investigations were conducted in the following procedures.
-Microstructure observation on the RPV clad(OEM,SEM,TEM)
-Inv

To use the small specimen techniques for evaluating the microstructural and mechanical property changes on nuclear reactor pressure vessel cald with neutron irradiation, the investigations were conducted in the following procedures.
-Microstructure observation on the RPV clad(OEM,SEM,TEM)
-Investigation of irradiation-induced microstructural changes
-Small tensile test before and after neutron irradiation
-Set up SP test cell and low temperature test facilities
Perform SP test from room temperature to liquid nitrogen temperature
-Analysis of SP transition behaviors with test temperatures and materials
-Comparison of SP properties between unirradiated and irradiated RPV clad
-SP specimen fracture surface observation

목차 Contents

• 제1장 서론...17
• 제2장 국내외 기술개발 현황...19
• 제1절.소형시험법 기술(Small specimen techniques)-소형펀치(small punch)시험...19
• 1.소형펀치 시험법(Small Punch test)...19
• 2.인장 특성과의 비교...20
• 3.Charpy 충격시험과의 관련성...21
• 제2절. 원자로 압력용기 클래드부의 열화현상...22
• 1.중성자 조사에 의한 취화...22
• 2.열시효 취화...23
• 제3장 실험절차...31
• 제1절 시험재료 제작...31
• 제2절 시편가공...31
• 제3절 시험 장비 및 미세조직 관찰...32
• 제4절 SP 시험 장치의 제작...32
• 제5절 온도측정 및 저온 유지...33
• 제6절 중성자 조사...33
• 제4장 실험결과 및 토의...42
• 제1절 미세조직 관찰...42
• 제2절 인장시험...43
• 제3절 소형펀치(SP)시험...44
• 1.비조사SP 시험결과와 인장성질의 관련성...44
• 2.조사후 SP 시험결과...48
• 제4절 SP 시편 파면 관찰...49
• 제5장 결론...50
• 제6장 연구개발결과 활용 및 향후연구계획...52
• 제7장 해외 과학기술 정보...53