○ The PAN electrospun membrane showed significantly higher ionic conductivity (0.64 mS/cm) than that of the PVdF electrospun membrane (0.21 mS·cm^-1) at 30 °C. By control of vapor area, the PAN electrospun membrane showed higher ionic conductivity (1.1 mS/cm) and high potential s

Result
○ The PAN electrospun membrane showed significantly higher ionic conductivity (0.64 mS/cm) than that of the PVdF electrospun membrane (0.21 mS·cm^-1) at 30 °C. By control of vapor area, the PAN electrospun membrane showed higher ionic conductivity (1.1 mS/cm) and high potential stability over 4.5 V (versus Li⁺/Li).
○ The electrolyte using IL by preparation of Germany research has high interface resistance over 500Ω and ionic conductivity of 6.5X10^-4 S/cm. The interface resistance was increasing with cycle.
○ The PAN electrospun membrane with the nano size SiO₂ by coating showed significantly higher ionic conductivity of 3.6 mS/cm with EC-DEC-NaPF₆ and 1.2 mS/cm with TERGME-NaCF₃SO₃ at 30 °C. By control of vapor area, the battery using the membrane showed high capacity and good cycleability, but We didn’t have long cycle life.

(출처 : SUMMARY 6p)

목차 Contents

• 표지 ... 1제출문 ... 2보고서 요약서 ... 3요약문 ... 4SUMMARY ... 6CONTENTS ... 7목차 ... 8제1장 연구개발과제의 개요 ... 9 1. 연구개발의 목적 ... 9 2. 연구개발의 필요성 ... 10 3. 연구개발의 범위 ... 10제2장 국내외 기술개발 현황 ... 11제3장 연구개발수행 내용 및 결과 ... 13 1. 연구개발의 내용 ... 13 2. 연구개발의 결과 ... 13제4장 목표달성도 및 관련분야에의 기여도 ... 20제5장 연구개발결과의 활용계획 ... 20제6장 연구개발과정에서 수집한 해외과학기술정보 ... 21제7장 연구시설ㆍ장비 현황 ... 21제8장 참고문헌 ... 21끝페이지 ... 22