Steady-state anodic and cathodic polarization curves were developed for the Al electrode in 60 mole %$AlCl_3$-40 mole % NaCl at $180^{\circ}C$$453^{\circ}K$). Ohmic resistance contributed substantially to the anodic polarization at current densities greater than 50 m...

Steady-state anodic and cathodic polarization curves were developed for the Al electrode in 60 mole %$AlCl_3$-40 mole % NaCl at $180^{\circ}C$$453^{\circ}K$). Ohmic resistance contributed substantially to the anodic polarization at current densities greater than 50 mA/$CM^2$ even with capillary tip placed close to the electrode. This could not be rationalized from the resistivity of the melt, which would lead to a much smaller polarization. It was therefore concluded that a layer of high resistance $AlCl_3$ (or $AlCl_3$-rich melt) formed close to the anode surface. From the IR-corrected anodic Tafel and Allen-Hickling plots an apparent anodic charge-transfer coefficient of ${\alpha}_a$ = (2.3 RT/F)(d log i/d${\eta}$) = $1.5{\pm}0.25$ was obtained. At cathodic current densities greater than approximately 30 mA/$cm^2$, slow ion diffusion and dendrite growth both interfered with the measurement of kinetic parameters.