ZrO2 powders having high purity were prepared from domestic zircon sand using the caustic fusion method and the soda ash sintering process. In the caustic fusion method, ZrO2 recovery was reached to 96% when 100/140 mesh zircon was reacted with NaOH at the NaOH/Zircon mole ratio 6 and at 650$^{...

ZrO2 powders having high purity were prepared from domestic zircon sand using the caustic fusion method and the soda ash sintering process. In the caustic fusion method, ZrO2 recovery was reached to 96% when 100/140 mesh zircon was reacted with NaOH at the NaOH/Zircon mole ratio 6 and at 650$^{\circ}C$ for 2 hours. And in the soda ash sintering process, ZrO2 was recovered to 88.5% when -325 mesh zircon was reacted with Na2CO3 at the Na2CO3/Zircon mole ratio 1.1 and 1050$^{\circ}C$ for 2 hours. In both cases, Zr component was extracted to ZrOCl2, subsequently crystallized to ZrOCl2$.$8H2O to increase the purity, and converted to ZrO2 by precipitation. And to increase the sinter ability of powder, Cl- ion was removed and strong agglomeration was avoided by methanol distribution of Zr(OH)4 precipitates.