Boehmite Sol-Gel법에 의한 $\\alpha$-Al2O3 분말제조시 Seeding 효과 Effect of Seeding on Preparation of $\\alpha$-$\\alpha$-Al2O3 Powders by Boehmite Sol-Gel Process원문보기
${\alpha}$-Al2O3 powder was produced at 1000$^{\circ}C$ by the boehmite sol-gel process with seeding 2 wt% ${\alpha}$-Al2O3. The processes and mechanisms of fornation of ${\alpha}$-Al2O3 was investigated using DTA/TG, XRD, TR spectroscopy and thermodynamic...
${\alpha}$-Al2O3 powder was produced at 1000$^{\circ}C$ by the boehmite sol-gel process with seeding 2 wt% ${\alpha}$-Al2O3. The processes and mechanisms of fornation of ${\alpha}$-Al2O3 was investigated using DTA/TG, XRD, TR spectroscopy and thermodynamic analysis. The specific surface area of the obtained ${\alpha}$-Al2O3 was 16.3㎡/g.
${\alpha}$-Al2O3 powder was produced at 1000$^{\circ}C$ by the boehmite sol-gel process with seeding 2 wt% ${\alpha}$-Al2O3. The processes and mechanisms of fornation of ${\alpha}$-Al2O3 was investigated using DTA/TG, XRD, TR spectroscopy and thermodynamic analysis. The specific surface area of the obtained ${\alpha}$-Al2O3 was 16.3㎡/g.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.