$SrTiO_3$powders were synthesized from the chloride and the nitrate aqueous solution by spray pyrolysis method using ultrasonic vibrator. The concentration of mother solution was prepared 0.05M and O.lM. The carrier gas flow rate was 0.5cm/sec and 1.5cm/sec, respectively. The formation pr...

$SrTiO_3$powders were synthesized from the chloride and the nitrate aqueous solution by spray pyrolysis method using ultrasonic vibrator. The concentration of mother solution was prepared 0.05M and O.lM. The carrier gas flow rate was 0.5cm/sec and 1.5cm/sec, respectively. The formation processing was investigated in the 0.05M and 0.05cm/sec. The $SrTiO_3$powders could not be synthesized from chloride aqueous solution. The prepared powders from nitrate aqueous solution was SrTi03 with cubic structure and nearly sphere particle for all samples. Mean particle size was increased from $0.49{\mu}m$ to $0.67{\mu}m$ by changing the carrier gas flow rate from O.5cm/sec to 1.5cm/sec. Also, mean particle size increased from $0.49{\mu}m$to $0.55{\mu}m$by changing the concentration of mother solution from O.05M to O.1M. Atomizing droplet size was $14.3{\mu}m$. The shape of particles was very porous by evaporation of solvent at the initial step. But through the each step upwards, shape of particles was formed themselves into a nearly roundish.