Four distinctive hot pressed and heat treated S${i_3}{N_4}$ceramics, S${i_3}{N_4}$-8%${Y_2}{O_3}$, S${i_3}{N_4}$-6% ${Y_2}{O_3}$-2% $A{l_2}{O_3}$, S${i_3}{N_4}$-4% ${Y_2}{O_3}$-3% $A{l_2}{O_3}$, 그리고 S<...

Four distinctive hot pressed and heat treated S${i_3}{N_4}$ceramics, S${i_3}{N_4}$-8%${Y_2}{O_3}$, S${i_3}{N_4}$-6% ${Y_2}{O_3}$-2% $A{l_2}{O_3}$, S${i_3}{N_4}$-4% ${Y_2}{O_3}$-3% $A{l_2}{O_3}$, 그리고 S${i_3}{N_4}$-1% MgO-1% Si$O_2$(in wt%), were prepared and characterized by X-ray diffraction, scanning electron microscopy, image analysis and mechanical tests. The fracture toughness of S${i_3}{N_4}$-8% ${Y_2}{O_3}$specimens containing large elongated grains showed the highest value of about 9.8MPa$m^{1/2}$. Two out of four S${i_3}{N_4}$, ceramics(S${i_3}{N_4}$-6% ${Y_2}{O_3}$-2% $A{l_2}{O_3}$and S${i_3}{N_4}$-4% ${Y_2}{O_3}$-3% $A{l_2}{O_3}$) heat treated at 200 $0^{\circ}C$retained the fracture strength of over 900MPa and fracture toughness of over 8.0MPa$m^{1/2}$. Large ${\beta}$-S${i_3}{N_4}$grains having a diameter larger than 1${\mu}$m appeared to contribute to increase in fracture toughness.