Room-temperature photoluminescent porous Si has been formed by etching Si wafer u-ith the solution of $HF:HNO_{3}: H_{2}O$=l : 5 : 10. We have observed photoluminescence(PL) spectra similar to those reported recently for porous-Si films formed by anodic etching with HF solutions. We have ...

Room-temperature photoluminescent porous Si has been formed by etching Si wafer u-ith the solution of $HF:HNO_{3}: H_{2}O$=l : 5 : 10. We have observed photoluminescence(PL) spectra similar to those reported recently for porous-Si films formed by anodic etching with HF solutions. We have also investigated the dependence of PI, spectra on the etching time which was varied from 1 to 10 minutes. We found that 5-minute etching gave us the strongest PL intensity. We also found by atomic force microscopy( AFM) measurements that the surface fearure size became smaller for longer etching time and the average feature size of the etched Si wafer for 5-minute was about 1, 500~2, 000$\AA$. This indicates that the surface feature of the etched porous Si affects the PL intensity of the sample.