논문 상세정보

고속 열 확산에 의한 얕은 접합 형성과 Ti-실리시이드화된 $n^+$ -p 다이오드 특성 분석

The Formation of the Shallow Junction by RTD and Characteristic Analysis for $n^+$ -p Diode with Ti-silicide

Abstract

The ultra shallow junction was formed by 2-step RTP. Phosphorus solid source(P$_{2}O_{5}$) was transfered on wafer surface during RTG(Rapid Thermal Glass Transfer) of which process condition was 80$0^{\circ}C$ and 60sec. The process temperature and time of the RTD(Rapid Thermal Diffusion) were 950~105$0^{\circ}C$ during 5~15sec respectively sheet resistances were measured as 175~320$\Omega$/m and junction depth and dopth and dopant surface concentration were measured as 0.075~0.18$\mu$m and 5${\times}10^{19}cm^{4}$ respectively. Ti-silicide was formed by 2-step RTA after 300$\AA$ Titanium was deposited. The 1st RTA (2nd RTA) was carried out at the temperature of $600^{\circ}C$(700~80$0^{\circ}C$) for 30 seconds (10~60 seconds) under N$_2$ ambient. Sheet resistances after 2nd RTA were measured as 46~63$\Omega$/D. Si/Ti component ratio was evaulated as 1.6~1.9 from Auger depth profile. Ti-Silicided n-p junction diode (pattern size : 400$\times$400$\mu$m) was fabricated under the RTD(the process was carried out at the temperature of 100$0^{\circ}C$ for 10seconds) and 2nd RTA(theprocess was carried out at the temperature of 750$^{\circ}C$ for 60 seconds). Leakage current was measured 1.8${\times}10^{7}A/mm^{2}$ at 5V reverse voltage. Whent the RTD process condition is at the temperature of 100$0^{\circ}C$ for 10seconds and the 2nd RTA process condition is at the temperature of 75$0^{\circ}C$ for 60 seconds leakage current was 29.15${\times}10^{9}A$(at 5V).

참고문헌 (0)

  1. 이 논문의 참고문헌 없음

이 논문을 인용한 문헌 (0)

  1. 이 논문을 인용한 문헌 없음

원문보기

원문 PDF 다운로드

  • ScienceON :

원문 URL 링크

원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다. (원문복사서비스 안내 바로 가기)

상세조회 0건 원문조회 0건

DOI 인용 스타일