The growth and characterization of heteroepitaxial $Si_{1-x}Ge_{x}$ films grown by the RTCVD (Rapid Thermal Chemical Vapor Deposition) method were described. For the growth of $Si_{1-x}Ge_{x}$ heteroepitaxial layers, $SiH_{4}$ / $GeH_{4}$ / $H_{2}$

The growth and characterization of heteroepitaxial $Si_{1-x}Ge_{x}$ films grown by the RTCVD (Rapid Thermal Chemical Vapor Deposition) method were described. For the growth of $Si_{1-x}Ge_{x}$ heteroepitaxial layers, $SiH_{4}$ / $GeH_{4}$ / $H_{2}$ gas mixtures were used. The growth conditions were varied to investigate their effects on the Si / Ge composition ratios, the interface abruptness and crystalline properties. The experimental data shows that the misfit threading dislocation in $Si_{1-x}Ge_{x}$ / Si heteroepitaxial film of about $400\;{\AA}$ thickness was not observed at the growth temperature of as low as $650^{\circ}C$, and the composition ratios of Si / Ge changed linearly with $SiH_{4}$ / $GeH_{4}$ gas mixing ratios in our experimental ranges. In the in-situ boron doping experiments, the doping abruptness would be controlled within several hundreds ${\AA}$/decade.