Various $TiO_2-SiO_2$ composite powders were prepared by the modified sol-gel method using 1-dodecanol as DCCA (Dryng Control Chemical Additive ). Their characterizations were carried out and their photocatalytic catalysis was examined on the evolution reaction of hydrogen. The weight los...

Various $TiO_2-SiO_2$ composite powders were prepared by the modified sol-gel method using 1-dodecanol as DCCA (Dryng Control Chemical Additive ). Their characterizations were carried out and their photocatalytic catalysis was examined on the evolution reaction of hydrogen. The weight losses at $500^{\circ}C$ of only $TiO_2$ and $SiO_2$ powders were 33. 0wt% and 42.5wt%, respectively, and those of the $TiO_2/SiO_2$ powders ($TiO_2/SiO_2=25/75$, 50/50 and 75/25) were about $70.0{\pm}3.0wt%$. The released substances from the powders were almost organic matters. The as-prepared powders except only $TiO_2$ powder were amorphous. Transformation of anatase to rutil was hindered by $SiO_2$ component and the crystallinity of anatase was decreased with increasing $SiO_2$ contents. The as-prepared powders were bulky states. By heating at $600^{\circ}C$ for 1 hr $TiO_2-SiO_2$ powders ($TiO_2=100%$, $TiO_2/SiO_2=75/25,\;50/50$) showed agglomerates consisted of particles in submicron, but those of $TiO_2/SiO_2=25/75$ and $SiO_2=100%$ were still bulky states. Specific surface area of the powders heat-treated at $600^{\circ}C$ for 1hr was increased with $SiO_2$ concents and their pore sizes were also depended on $SiO_2$ contents. The photocatalytic activity of $TiO_2/SiO_2=75/25$ heat-treated at $600^{\circ}C$ for 1hr was 0.240mo1/h.g-cat as $H_2$ evolution rate. This value was about 2.0 times that of P-25(Degussa P-25) as a standard photocatalyst.