Various $Cu/SiO_2$ catalysts with copper concentration ranging from 0 to 50wt% were prepared by kneading method for the steam reforming of methanol. These catalysts were calcined at temperatures in the range of $400^{\circ}C{\sim}900^{\circ}C$ and then reduced in a $H_2$

Various $Cu/SiO_2$ catalysts with copper concentration ranging from 0 to 50wt% were prepared by kneading method for the steam reforming of methanol. These catalysts were calcined at temperatures in the range of $400^{\circ}C{\sim}900^{\circ}C$ and then reduced in a $H_2$ atmosphere in the range of $150^{\circ}C{\sim}350^{\circ}C$. Steam reforming of methanol was carried out at atmospheric pressure over a temperature range of $200^{\circ}C{\sim}400^{\circ}C$, steam/methanol molar ratio of 0.4~1.6 and W/F of 3~25 g.-cat.hr./mol. Characterization of the catalysts was studied using IR, BET and XRD. Using copper nitrate as a precursor for catalysts, pH in the preparation of catalysts had a great effect on the catalytic activity, but pH in the preparation of catalysts, calcination temperature, and reducing temperature in $H_2$ atmosphere had no effect on the product distribution. Optimum copper concentration, calcination temperature and reducing temperature were 40wt%, $700^{\circ}C$ and $300^{\circ}C$, respective)y. Reaction temperature for maximum $H_2$ production was $275^{\circ}C$, and the formation of methane which lowered quantity and quality of $H_2$ would be inhibited below $275^{\circ}C$. $Cu^{\circ}-Cu_2O$ might be active species in $Cu/SiO_2$ catalyst.