The effects of epoxy resins and content of catalyst on the cure characteristics were studied by FT-IR, DSC and dynamic viscometer for the thermal properties and rheological properties of the catalytic (N-Benzylpyrazinium hexafluoroantimonate, BPH) epoxy thermosetting system. Compared with DSC result...

The effects of epoxy resins and content of catalyst on the cure characteristics were studied by FT-IR, DSC and dynamic viscometer for the thermal properties and rheological properties of the catalytic (N-Benzylpyrazinium hexafluoroantimonate, BPH) epoxy thermosetting system. Compared with DSC results of DEGBF containing 0.5wt% BPH, the DSC thermograms of DGEBA containing 0.5wt% BPH indicated that the reaction was faster than that of DGEBF/BPH and the conversion rate of DGEBA/BPH was high in the initial stage of the reaction. As the concentration of BPH increases, the reaction and conversion rates show similar value in both the cases. The influence of hydroxyl group of epoxy resin on gel point defined from the crossover point of storage modulus (G') and loss modulus (G") could be explained by the formation of 3-dimensional network in the initial stage owing to the curing reaction between epoxides and hydroxyl groups of epoxy resin. This was consistent with the gel point obtained from DSC, FT-IR and moduli crossover. The activation energy (Et) obtained from the crossover point (G'/G"=1) are $31-39kJ.mol^{-1}$ for various BPH compositions in case of two epoxy systems.