High temperature thermal behaviors of EAF dust by coke at initial reaction stage were studied to obtain the fundamental data of EAF dust treatment process, that is Extended Arc Plasma Furnace System called RAPID system. In this study thermal behaviors including calcination of limestone, devolatiliza...

High temperature thermal behaviors of EAF dust by coke at initial reaction stage were studied to obtain the fundamental data of EAF dust treatment process, that is Extended Arc Plasma Furnace System called RAPID system. In this study thermal behaviors including calcination of limestone, devolatilization of EAF dust itself, and reduction & devolatilization of mixture(EAF dust : coke : limestone = 80 : 10 : 10 wt.%) were investigated as functions of reaction temperature (1000~1300$^{\circ}C$) and reaction time (3~12 min), considering the 180% equivalence of carbon reduction and 1.7 bacisity for optimum reduction and melting of EAF dust in the RAPID system. Size of sample was about below 0.1 mm for these experiments. Limestone was completely calcined at above 1100$^{\circ}C$ within 1 minutes. In the case of devolatilization of EAF dust itself, weight loss of EAF dust was about 14% at 1300$^{\circ}C$ and 12 minutes, and partial sintering and melting were found in part of sample. Weight loss of mixtures increased with increasing reaction temperature and time, about 46% weight loss in it was occurred at 1300$^{\circ}C$ and 12 minutes. From these weight losses showing devolatilization and reduction of EAF dust, the treatment time of EAF dust inside.

주제어