When sulfuric acid was added in HCl etching solution, corrosion of aluminum metal was inhibited by the chemical adsorption of sulfate ions. In the presence of $SO_4^{-2}$, cyclic voltammetry showed that the protective oxide film was formed on the inner surfaces of etch pits and, pit densi...

When sulfuric acid was added in HCl etching solution, corrosion of aluminum metal was inhibited by the chemical adsorption of sulfate ions. In the presence of $SO_4^{-2}$, cyclic voltammetry showed that the protective oxide film was formed on the inner surfaces of etch pits and, pit density was increased by nucleation on both the aluminum surface and the pits inside. Structure and distribution of etch pits found in AC etching of aluminum were strongly influenced by the concentration of $SO_4^{-2}$ and the amount of cathodic pulse charging. Below $0.8mC/cm^2$ of cathodic pulse charging, oxide films formed inside actively dissolving pits indicated the higher resistance to pit nucleation as the concentration of $SO_4^{-2}$ increases. However, the structural change of oxide films occurred above the $0.8mC/cm^2$ charging and the effect of $SO_4^{-2}$ was minimized, and it resulted in the rapid formation of etch pits.

주제어