Pt/C powder which was used as electrocatalyst in a Phosphoric Acid Fuel Cell(PAFC) was fabricated by colloid method. It was reported that the sulfur from reductant, $Na_2S_2O_4$, worked as a poison against catalyst during long term operation. To remove these sulfurs, we try to treat Pt/C ...

Pt/C powder which was used as electrocatalyst in a Phosphoric Acid Fuel Cell(PAFC) was fabricated by colloid method. It was reported that the sulfur from reductant, $Na_2S_2O_4$, worked as a poison against catalyst during long term operation. To remove these sulfurs, we try to treat Pt/C powder by three different methods. First, we tried to remove the sulfur according to temperature and time in $H_2$ atmosphere. As the heat treatment temperature is raised up, the effect of the removal is increased but the electrode performance is decreased because of the growth of Pt particle size. The optimal heat treatment temperature is $400^{\circ}C$, the size of Pt particle is approximately $35{\sim}40{\AA}$ and the electrode performance is $360mA/cm^2$ at 0.7 V. At $400^{\circ}C$, even though the time of heat treatment is extended, size of Pt, amounts of remaining sulfur and electrode performance is almost constant. Secondly, when we removed in a crucible at $900^{\circ}C$ the removal of the sulfur was not better, but the size of Pt particle, approximately $80{\AA}$, was smaller than that of heat treatment in $H_2$ atmosphere at $900^{\circ}C$. Lastly we treated with solvents such as acetone, benzene, and carbon disulfide. It was observed that sulfur components were removed partly by extraction with solvents, the electrode performances were similar each other.

주제어