In this study, binary polyamide 6,6(PA 6,6)/ethylene-propylene rubber(EPM) or EPM-g-maleic anhydride(EPM-g-MA) blends and ternary PA 6,6/EPM/EPM-g-MA blends with various elastomer content were prepared in order to investigate the degree of influence of elastomer content and average particle size, mo...

In this study, binary polyamide 6,6(PA 6,6)/ethylene-propylene rubber(EPM) or EPM-g-maleic anhydride(EPM-g-MA) blends and ternary PA 6,6/EPM/EPM-g-MA blends with various elastomer content were prepared in order to investigate the degree of influence of elastomer content and average particle size, morphology, and distribution of dispersed elastomer on mechanical and thermal properties of blends. According to the results, notched Izod impact strength and relative crystallinity of binary blends modified with EPM-g-MA as well as average particle size and distribution of dispersed elastomer in such blends were more improved than those of binary blends modified with EPM. Notched Izod impact strength of blend whose composition ratio(wt % ) was 70:30(PA 6,6 : EPM-g-MA) was the highest among the binary PA 6,6/EPM-g-MA blends. The impact strength was increased by 25 times and its relative crystallinity was increased by 7 times when compared with those of polyamide 6,6. In the case of ternary PA 6,6/EPM/EPM-g-MA blend of which composition ratio was 70:15:15(PA 6,6:EPM:EPM-g-MA), the elastomer was finely distributed with the average particle size of $0.56{\mu}m$. The Izod impact strength of this blend was the highest of all blends prepared with different elastomer content.

주제어