Aluminum dross should be recycled in consideration of characteristics of the dross and its reutilization after processing. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing aluminum hydroxide. Sample dross was cl...

Aluminum dross should be recycled in consideration of characteristics of the dross and its reutilization after processing. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing aluminum hydroxide. Sample dross was classified according to its size. The dross smaller than $850\mu$m was leached with sodium hydroxide solution to extract the remaining aluminum from the dross into the solution, and then aluminum hydroxide precipitate was recovered (rom the leach liquor. Purity of the obtained aluminum hydroxide was above 98% and size of the sample was in range of $\3~39mu$m. Recovery of aluminum hydroxide precipitate was highest on condition that A/C ratio of the solution was 0.5 and pulp density was 14~16% at the leaching step. From the result, it was suggested that this process could be applicable to recycling of aluminum dross.

주제어