Poly(trimethylene terephthalate)(PTT) fibers were treated by passing on the plate heater to study the annealing effect on the change of morphological structure and physical properties. In the X-ray diffraction curves of PTT annealed, a sharp peak at 2$\theta$=15.6$^{\circ}$ app...

Poly(trimethylene terephthalate)(PTT) fibers were treated by passing on the plate heater to study the annealing effect on the change of morphological structure and physical properties. In the X-ray diffraction curves of PTT annealed, a sharp peak at 2$\theta$=15.6$^{\circ}$ appeared and the peak intensity became stronger with the increase of annealing temperature and time. This peak was based on the (010) plane of PTT crystals. The crystallinity determined by density measurement was also increased by annealing. With the increases of temperature and time, the dynamic viscoelastic behaviors were shown to be a large reduction in T(tan $\delta$$_{max}$). The birefringence and $T_g$ were also reduced, but the melting temperature was the same. These results mean that the molecular chains in armorphous region are transfered into the crystalline legion, making the remained chains relaxed during annealing at tensionless state.

주제어