ZnWO$_4$shows excellent frequency selectivity due to its high quality factor(Q${\times}$f) at microwave frequencies. However, in order to use ZnWO$_4$as multilayered wireless communication components, its other properties such as sintering temperature(105$0^{\ci...

ZnWO$_4$shows excellent frequency selectivity due to its high quality factor(Q${\times}$f) at microwave frequencies. However, in order to use ZnWO$_4$as multilayered wireless communication components, its other properties such as sintering temperature(105$0^{\circ}C$). $$\tau$_f$(-70ppm/$^{\circ}C$) and $$\varepsilon$_r$(15.5) should be modified. In present study, TiO$_2$and LiF were used to improve the microwave dielectric and sintering properties of ZnWO$_4$. TiO$_2$ additions to ZnWO$_4$changed $\tau$$_{f}$ from negative to positive value, and also increased $$\varepsilon$_r$, due to its high $$\tau$_f$(＋400ppm$^{\circ}C$) and $$\varepsilon$_r$(100). At 20 mol% TiO$_2$ addition, $$\tau$_f$was controlled to near zero ppm/$^{\circ}C$ with $$\varepsilon$_r$=19.4 and Q${\times}$ f=50000GHz. However, the sintering temperature was 110$0^{\circ}C$. LiF addition to the ZnWO$_4$＋TiO$_2$ mixture greatly reduced the sintering temperature from 110$0^{\circ}C$ to 85$0^{\circ}C$ due to liquid phase formation. Also LiF addition decreased the $$\tau$_f$value due to its high negative $$\tau$_f$ value. Therefore, by controlling the TiO$_2$and LiF amount. temperature stable LTCC(Low Temperature Cofired Ceramics) material with low loss in the ZnWO$_4$-TiO$_2$-LiF system could be fabricated.d.d.

주제어