The wear of engine valve and seat insert is one of the most important factors which affect engine performance. Because of higher demands on performance and the increasing use of alternative fuel, engine valve and seat insert are challenged with greater wear problems than in the past. In order to sol...
The wear of engine valve and seat insert is one of the most important factors which affect engine performance. Because of higher demands on performance and the increasing use of alternative fuel, engine valve and seat insert are challenged with greater wear problems than in the past. In order to solve the above problems, a simulator was developed to be able to generate and control high temperatures and various speeds during motion. The wear simulator is considered to be a valid simulation of the engine valve and seat insert wear process with various speeds during engine activity. This work focuses on the different degrees of wear at three different singular test speeds (10 Hz, 25 Hz & multi-Hz). For this study, the temperature of the outer surface of the seat insert was controlled at 350$^{\circ}C$, and the test load was 1960 N. The test cycle number was $6.0{\times}10^6$. The mean ($\pm$standard error) wear depth of the valve at 10 Hz and 25 Hz was 45.1 ($\pm$3.7)$\mu$m and 81.7 ($\pm$2.5)$\mu$m, respectively. The mean wear depth of the seat insert at 10 Hz and 25 Hz was 52.7 ($\pm$3.9)$\mu$m and 91.2 ($\pm$2.7)$\mu$m, respectively. In the case of multi-Hz it was 70.7 ($\pm$2.4)$\mu$m and 77.4 ($\pm$3.8)$\mu$m, respectively. It was found that higher speed (25 Hz) cause a greater degree of wear than lower speed (10 Hz) under identical test condition (temperature, valve displacement, cycle number and test load). In the wear mechanisms of valves, adhesive wear, shear strain and abrasive wear could be observed. Also, in the wear mechanisms of seat inserts, adhesive wear, surface fatigue wear and abrasive wear could be observed.
The wear of engine valve and seat insert is one of the most important factors which affect engine performance. Because of higher demands on performance and the increasing use of alternative fuel, engine valve and seat insert are challenged with greater wear problems than in the past. In order to solve the above problems, a simulator was developed to be able to generate and control high temperatures and various speeds during motion. The wear simulator is considered to be a valid simulation of the engine valve and seat insert wear process with various speeds during engine activity. This work focuses on the different degrees of wear at three different singular test speeds (10 Hz, 25 Hz & multi-Hz). For this study, the temperature of the outer surface of the seat insert was controlled at 350$^{\circ}C$, and the test load was 1960 N. The test cycle number was $6.0{\times}10^6$. The mean ($\pm$standard error) wear depth of the valve at 10 Hz and 25 Hz was 45.1 ($\pm$3.7)$\mu$m and 81.7 ($\pm$2.5)$\mu$m, respectively. The mean wear depth of the seat insert at 10 Hz and 25 Hz was 52.7 ($\pm$3.9)$\mu$m and 91.2 ($\pm$2.7)$\mu$m, respectively. In the case of multi-Hz it was 70.7 ($\pm$2.4)$\mu$m and 77.4 ($\pm$3.8)$\mu$m, respectively. It was found that higher speed (25 Hz) cause a greater degree of wear than lower speed (10 Hz) under identical test condition (temperature, valve displacement, cycle number and test load). In the wear mechanisms of valves, adhesive wear, shear strain and abrasive wear could be observed. Also, in the wear mechanisms of seat inserts, adhesive wear, surface fatigue wear and abrasive wear could be observed.
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
제안 방법
,e and seat insert, under conditions similar to those of a vehicle engine, using a simulator which could change speed (Hz) during motion. In this study, tests have been conducted using three speeds (10 Hz, 25 Hz, Multi-Hz) for the wear depth and wear mechanism of the val.,e and seat insert by means of a wear simulator with the identical test conditions similar to those of an actual vehicle engine.
참고문헌 (10)
Chun, K. J., Hong, J. S., Lee, H. J., Kim, D. Y. and Im, J. K., 2004, 'A Study on Engine Valve and Seat Insert Wearing Depending on Speed Change,' SAE Paper 2004-01-16
Dissel, R. van, Barber, G. C., Larson, J. M. and Narasimhan, S. L., 1989, 'Engine Valve Seat and Insert Wear,' SAE Paper 892146
Fujiki, A. and Kano, M., 1992, 'New PM Seat Insert Materials for High Performance Engines,' SAE Paper 920570
Kim, G. S., Lee, I. C. and Jeong, I. S., 1999, 'Fine Constitution and Mechanical Properties of Sintered seat insert for Gasoline Engine Depending on Ni and Mo Contents,' Korea Metal Society Journal, Vol. 37, No.6, pp. 694-699
Lewis, R., Dwyer-Joyce, R. S. and Josey, G., 1999, 'Investingation of Wear Mechanisms Occurring in Passenger Car Diesel Engine Inlet Valve and Seat Insert,' SAE Paper 1999-01-1216
Ootani, T., Yahata, N., Fujiki, A. and Ehira, A., 1995, 'Impact Wear Characteristics of Engine Valve and seat Insert Insert Materials at High Temperature (impact Wear Tests of Austenitic Heat-Resistant Steel SUH36 against Fe-Base ?Sintered Alloy Using Plane Specimens),' Wear 188, pp. 175-184
Pyle, W. R. and Smrcka, N. R., 1993, 'The Effect of Lubricating Oil Additive on Valve Recession in Stationary Gaseous-Fueled Four-Cycle Engine,' SAE 932780
Sato, K., Midorikawa, T., Takahashi, T. and Oshige, H., 2000, 'Development of Seat Insert Material for Gas-Fueled Engines', SAE Paper ?2000-01-0911
Scott, C. G., Riga, A. T. and Hong, H., 1995, 'The Erosion-Corrosion of Nickel-Base Diesel Engine Exhaust Valves,' Wear 181-183, pp. 485-494
Zhao, R., Barber, G. C., Wang, Y. S. and Larson, J. E., 1997, 'Wear Mechanism Analysis of Engine Exhaust Valve Seats with a Laboratory Simulator,' STLE, Vol. 40, No.2, pp.209-218
※ AI-Helper는 부적절한 답변을 할 수 있습니다.