NTIS 바로가기大韓機械學會論文集. Transactions of the Korean Society of Mechanical Engineers. A. A, v.30 no.10 = no.253, 2006년, pp.1219 - 1226
허남수 , 윤기봉 (중앙대학교 기계공학부) , 김윤재 (고려대학교 기계공학과)
The ASTM test standard recommends the use of the compact tension specimen for creep crack growth rates measurement. In the creep crack growth rate test, the displacement rate due to creep is obtained by subtracting the contribution of elastic and plastic components from the total load line displacem...
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
ASTM International, 1992, 'Standard Test Method for Measurement of Creep Crack Growth Rates in Metals,' ASTM Test Standard E1457-92
Saxena, A., 1998, 'Nonlinear Fracture Mechanics for Engineers', ERC Press
Saxena, A, Han, J. and Banerji, K., 1988, 'Creep Crack Growth Behavior in Power Plant Boiler and Steam Pipe Steels,' ASME Journal of Pressure Vessel Technology, Vol. 110, pp. 137-146
Yoon, K.B., Saxena, A. and McDowell, D.L., 1992, 'Influence of Crack-Tip Cyclic Plasticity on Creepatigue Crack Growth,' Fracture Mechanics: Twenty Second Symposium, Vol. 1, ASTM STP 1131, pp. 367-392
Kim, YJ., Huh, N.S. and Kim, YJ., 2001, 'Effect of Liiders Strain on Engineering Crack Opening Displacement Estimations: Finite Element Study,' Fatigue and Fracture of Engineering Materials and Structures, Vol. 24, pp. 617-624
Rahman, S., Brust, F., Ghadiali, N. and Wilkowski, G, 1998, 'Crack-Opening-Area Analyses for Circumferential Through-Wall Cracks in Pipes-Part II: Model Validation,' International Journal of Pressue Vessels and Piping, Vol. 75, pp. 375-396
Webster, GA. and Ainsworth, R.A., 1994, 'High Temperature Component Life Assessment,' Chapman & Hall, London
Riedel, H., 1987, 'Fracture at High Temperature,' Springer-Verlag, Berlin
Ainsworth, R.A., 1993, 'The Use of a Failure Assessment Diagram for Initiation and Propagation of Defects at High Temperatures,' Fatigue and Fracture of Engineering Materials and Structures, Vol. 16, pp. 1091-1108
Ainsworth, R.A, Hooton, D.G and Green, D., 1999, 'Failure Assessment Diagrams for High Temperature Defect Assessment,' Engineering Fracture Mechanics, Vol. 62, pp. 95-109
Fookes, AI. and Smith, D.J., 2003, 'The Influence of Plasticity in Creep Crack Growth in Steels,' International Journal of Pressure Vessels and Piping, Vol. 80, pp. 453-463
Kumar, V., German, M.D. and Shih, C.F., 1981, 'An Engineering Approach for Elastic-Plastic Fracture Analysis,' EPRl NP-1931
Tada, H., 1973, 'The Stress Analysis of Cracks Handbook,' Paris Productions Inc
Norris, D.M. and Chexal, B., 1987, 'PICEP: Pipe Crack Evaluation Program,' EPRl NP 3596-SR
Scott, P., Olson, R., Marschall, C., Rudland, D., Francini, R., Wolterman, R., Hopper, A. and Wilkowski, G, 1996, 'Pipe System Experiments with Circumferential Cracks in Straight-Pipe Locations,' NUREG/CR-6389, USNRC
Kim, YJ., Huh, N.S., Kim, YJ., Choi, YH. and Yang, J.S., 2004, 'On Relevant Ramberg-Osgood Fit to Engineering Nonlinear Fracture Mechanics Analysis,' ASME Journal of Pressure Vessel Technology, Vol. 126, pp. 277-283
'ABAQUS User's manual,' ABAQUS, Inc., 2003
Kim, YJ., 1998, 'Note on Y/T vs. n for SlNTAP Procedure: Continuous and Dis-continuous Hardening,' In: Document generated within Brite-Euram Project 1426-Structural Integrity Assessment Procedures for European Industry - SlNTAP
Bannister, AC., Ruiz Ocejo, J. and Gutierrez-Solana F., 2000, 'Implications of the Yield Stress/Tensile Stress Ratio to the SlNTAP Failure Assessment Diagrams for Homogeneous Materials,' Engineering Fracture Mechanics, Vol. 67, pp. 547-562
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.