Various additives were added in small amounts on Ni/YSZ anode of SOFC (solid oxide fuel cell) in order to improve reactivity and to inhibit deactivation due to coke deposition during methane reforming using a low mole ratio steam ($H_2O/CH_4=1.5$) at $800^{\circ}C$. Ni/YSZ cata...

Various additives were added in small amounts on Ni/YSZ anode of SOFC (solid oxide fuel cell) in order to improve reactivity and to inhibit deactivation due to coke deposition during methane reforming using a low mole ratio steam ($H_2O/CH_4=1.5$) at $800^{\circ}C$. Ni/YSZ catalysts added with various perovskites did not show any improvement but exhibited a gradual decrease in the methane conversion. K-doped Ni/YSZ showed a steady increase and maintenance of the conversion up to 42 hours, after which there was an abrupt deactivation of catalyst owing to potassium loss by volatilization. Addition of 5% of $K_2Ti_2O_5$ on Ni/YSZ showed a stable maintenance of the conversion without K loss, and was able to prevent coke formation during a long time operation. Deactivation of catalyst during the reaction was mainly caused by the accumulation of graphidic carbon on the catalyst surface.

주제어