Aminopropyl Triethoxysilane과 아크릴 단량체를 이용한 Silylated Acrylic Polyurethane Dispersion의 제조 Preparation of Silylated Acrylic Polyurethane Dispersion Using Aminopropyl Triethoxysilane and Acrylate Monomers원문보기
Waterborne polyurethane dispersion (PUD) was synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate, polycarbonate diol and dimethylol propionic acid, with aminopropyl triethoxysilane (APS). Subsequently, silylated acrylic polyurethane dispersion was...
Waterborne polyurethane dispersion (PUD) was synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate, polycarbonate diol and dimethylol propionic acid, with aminopropyl triethoxysilane (APS). Subsequently, silylated acrylic polyurethane dispersion was synthesized by reacting the PUD with the mixture of acrylate monomers, 2-hydroxyethyl methacrylate and methyl methacrylate. The average particle size of silylated acrylic polyurethane dispersion, measured by the dynamic light scattering method, was increased from 39.0 nm to 399.8 nm by increasing the addition amounts of APS. Also, the pencil hardness of coating films of silylated acrylic polyurethane dispersion was enhanced from B grade to F grade with increasing APS content.
Waterborne polyurethane dispersion (PUD) was synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate, polycarbonate diol and dimethylol propionic acid, with aminopropyl triethoxysilane (APS). Subsequently, silylated acrylic polyurethane dispersion was synthesized by reacting the PUD with the mixture of acrylate monomers, 2-hydroxyethyl methacrylate and methyl methacrylate. The average particle size of silylated acrylic polyurethane dispersion, measured by the dynamic light scattering method, was increased from 39.0 nm to 399.8 nm by increasing the addition amounts of APS. Also, the pencil hardness of coating films of silylated acrylic polyurethane dispersion was enhanced from B grade to F grade with increasing APS content.
Shin, Y. T., Hong, M. G., Choi, J. J., Lee, W. K., Lee, G. B., Yoo, B. W., Lee, M. G. and Song, K. C., "Preparation and Properties of Aminosilane Terminated Waterborne Polyurethane," Korean Chem. Eng. Res. (HWAHAK KONGHAK), 48(4), 434-439(2010).
Kim, S. M., Kwak, N. S., Yang, W. K., Lim, B. K., Park, B. Y. and Hwang, T. S., "Synthesis and Physical Properties of Polycaprolactone Based Polyurethanes Using Aliphatic or Aromatic Diisocyanates," Polymer(Korea), 29(3), 253-259(2005).
Hong, M. G., Shin, Y. T., Choi, J. J., Lee, W. K., Lee, G. B., Yoo, B. W., Lee, M. G. and Song, K. C., "Preparation of Silylated Waterborne Polyurethane/Silica Nanocomposites Using Colloidal Silica," Korean Chem. Eng. Res. (HWAHAK KONGHAK), 48(5), 561-567(2010).
Shin, Y. T., Hong, M. G., Choi, J. J., Lee, W. K., Yoo, B. W., Lee, M. G. and Song, K. C., "Effect of Addition of Pentaerythritol Triacrylate on the Properties of Waterborne Polyurethane," Korean Chem. Eng. Res. (HWAHAK KONGHAK), 49(4), 411-416(2011).
Kim, B. S., Hong, M. G., Yoo, B. W., Lee, M. G. and Song, K. C., "Effect of Types of Acrylate Monomers on the Properties of Waterborne Polyurethane-Acrylic Hybrid Solutions," Korean Chem. Eng. Res. (HWAHAK KONGHAK), 50(3), in press(2012).
ASTM D 3359, "Standard Test Methods for Measuring Adhesion by Tape Test," ASTM International, 927-929(1997).
Hwang, J. H. and Song, K. C., "Preparation of UV-Curable Organic-Inorganic Hybrid Coatings Using Alumina Sols and Acrylate Monomers," Korean Chem. Eng. Res. (HWAHAK KONGHAK), 49(3), 277-284(2011).
※ AI-Helper는 부적절한 답변을 할 수 있습니다.