The branched copolyester was synthesized and its molecular weight, $T_g$, 1/2 method temperature ($T_{1/2}$) and rheological properties were characterized for the application of toner binder. The linear copolyester had low molecular weight and melt elasticity obtained by dimeth...
The branched copolyester was synthesized and its molecular weight, $T_g$, 1/2 method temperature ($T_{1/2}$) and rheological properties were characterized for the application of toner binder. The linear copolyester had low molecular weight and melt elasticity obtained by dimethylterephthalate (DMT), ethylene glycol (EG) and 2,2-bis(4-(2-hydroxypropoxy) phenyl)propane (HPP). The branched copolyesters prepared with various branching agents such as 2-(hydroxymethyl)-2-ethylpropane-1,3-diol (trimethylol propane, TMP), 2,2-bi(hydroxymethyl)-1,3-propanediol (pentaerythritol, PER), 1,2,4-benzenetricarboxylic anhydride (trimellitic anhydride, TMA) and glycerol to improve the physical properties of the linear copolyester. The effect of branching agents on the molecular weight and melt elasticity of the branched copolyester was examined. The branched copolyesters prepared by adding over 15 mol% of branching agent showed relatively high molecular weight and melt elasticity, and $T_{1/2}$ value of $140^{\circ}C$. Therefore, the highly branched copolyesters were deemed suitable as a hot-melt toner of laser print process.
The branched copolyester was synthesized and its molecular weight, $T_g$, 1/2 method temperature ($T_{1/2}$) and rheological properties were characterized for the application of toner binder. The linear copolyester had low molecular weight and melt elasticity obtained by dimethylterephthalate (DMT), ethylene glycol (EG) and 2,2-bis(4-(2-hydroxypropoxy) phenyl)propane (HPP). The branched copolyesters prepared with various branching agents such as 2-(hydroxymethyl)-2-ethylpropane-1,3-diol (trimethylol propane, TMP), 2,2-bi(hydroxymethyl)-1,3-propanediol (pentaerythritol, PER), 1,2,4-benzenetricarboxylic anhydride (trimellitic anhydride, TMA) and glycerol to improve the physical properties of the linear copolyester. The effect of branching agents on the molecular weight and melt elasticity of the branched copolyester was examined. The branched copolyesters prepared by adding over 15 mol% of branching agent showed relatively high molecular weight and melt elasticity, and $T_{1/2}$ value of $140^{\circ}C$. Therefore, the highly branched copolyesters were deemed suitable as a hot-melt toner of laser print process.
A. Pizzi, "Urea-Formaldehyde Adhesives", in Handbook of Adhesive Technology, A. Pizzi and K. L. Mittal, Editors, Marcel Dekker, New York, Chap. 31, p 478 (2003).
P. Bajaj and D. N. Khanna, Polym. J., 17, 275 (1981).
H. Kawaji and M. Maruta, Proceeding of IS&Ts NIP, 19,133 (2003).
W. S. Ha and D. M. Lee, Tex. Sci. Eng., 24,95 (1987).
T. Sakano, National Technical Report(Japan), 23, 415 (1977).
R. T. Agger, Adhesion, 13, 98 (1988).
N. Fukuri, E. Shirai, and K. Aoki, Proceeding of IS&Ts NIP, 23, 230 (2007).
T. Kubo, E. Shirai, and K. Aoki, Proceeding of IS&Ts NIP, 20, 73 (2004).
A. Toman, C. Provost, and J. Polley, Proceeding of IS&Ts NIP, 20, 78 (2004).
D. N. Bikiaris and G. P. Karayannidis, J. Polym. Sci., Polym. Chem. Ed., 34, 1337 (1996).
D. N. Bikiaris and G. P. Karayannidis, J. Polym. Sci., Polym. Chem. Ed., 33, 1705 (1995).
※ AI-Helper는 부적절한 답변을 할 수 있습니다.