NTIS 바로가기Journal of the Korean Recycled Construction Resources Institute = 한국건설순환자원학회 논문집, v.9 no.4, 2021년, pp.460 - 468
온정권 (무영CM 건축사사무소) , 김규용 (충남대학교 건축공학과) , 사수이 (충남대학교 건축공학과) , 이예찬 (충남대학교 건축공학과) , 유하민 (충남대학교 건축공학과)
Owing to the production of conventional concrete/cement, the climate crises is increasing and is mainly caused greenhouse gas (GHG) emission into the environment by industrial process. To reduce the emission of GHG, and excessive consumption of energy, research on geopolymer binder is increasing as ...
Abdul Rahim, R.H., Rahmiati, T., Azizli, K.A., Man, Z., Nuruddin, M.F., Ismail, L. (2015). Comparison of using NaOH and KOH activated fly ash-based geopolymer on the mechanical properties, Materials Science Forum, 803, 179-184.
Al Bakria, A.M., Kamarudin, H., BinHussain, M., Nizar, I.K., Zarina, Y., Rafiza, A.R. (2011). The effect of curing temperature on physical and chemical properties of geopolymers, Physics Procedia, 22, 286-291.
Bakharev, T. (2005). Durability of geopolymer materials in sodium and magnesium sulfate solutions, Cement and Concrete Research, 35(6), 1233-1246.
Bortnovsky, O., Dedecek, J., Tvaruzkova, Z., Sobalik, Z., Subrt, J. (2008). Metal ions as probes for characterization of geopolymer materials, Journal of the American Ceramic Society, 91(9), 3052-3057.
Breck, D.W., Breck, D.W. (1973). Zeolite molecular sieves: structure, chemistry, and use, John Wiley & Sons.
Chindaprasirt, P., Chalee, W. (2014). Effect of sodium hydroxide concentration on chloride penetration and steel corrosion of fly ash-based geopolymer concrete under marine site, Construction and Building Materials, 63, 303-310.
Chindaprasirt, P., Chareerat, T., Sirivivatnanon, V. (2007). Workability and strength of coarse high calcium fly ash geopolymer, Cement and Concrete Composites, 29(3), 224-229.
Davidovits, J. (1991). Geopolymers: inorganic polymeric new materials, Journal of Thermal Analysis and Calorimetry, 37(8), 1633-1656.
Davidovits, J. (2002). Years of successes and failures in geopolymer applications. Market trends and potential breakthroughs, Geopolymer 2002 Conference Saint-Quentin, France; Melbourne, Australia: Geopolymer Institute, 28, 29.
Davidovits, J. (2011). Calcium based geopolymer, Geopolymer Chemistry and Applications, 3rd ed., Geopolymer Institute, Saint Quentin, France, 201-244.
Diaz, E.I., Allouche, E.N., Eklund, S. (2010). Factors affecting the suitability of fly ash as source material for geopolymers, Fuel, 89(5), 992-996.
Duxson, P.S.W.M., Mallicoat, S.W., Lukey, G.C., Kriven, W.M., van Deventer, J.S. (2007). The effect of alkali and Si/Al ratio on the development of mechanical properties of metakaolin-based geopolymers, Colloids and Surfaces A: Physicochemical and Engineering Aspects, 292(1), 8-20.
Elyamany, H.E., Abd Elmoaty, M., Elshaboury, A.M. (2018). Magnesium sulfate resistance of geopolymer mortar, Construction and Building Materials, 184, 111-127.
Fang, G., Ho, W.K., Tu, W., Zhang, M. (2018). Workability and mechanical properties of alkali-activated fly ash-slag concrete cured at ambient temperature, Construction and Building Materials, 172, 476-487.
Gunasekara, C., Bhuiyan, S., Law, D., Setunge, S., Ward, L. (2017). Corrosion resistance in different fly ash based geopolymer concretes, HPC/CIC Tromso; Norway.
He, J., Jie, Y., Zhang, J., Yu, Y., Zhang, G. (2013). Synthesis and characterization of red mud and rice husk ash-based geopolymer composites, Cement and Concrete Composites, 37, 108-118.
Jamieson, E., McLellan, B., Van Riessen, A., Nikraz, H. (2015). Comparison of embodied energies of ordinary portland cement with bayer-derived geopolymer products, Journal of Cleaner Production, 99, 112-118.
Kani, E.N., Allahverdi, A. (2009). Effect of chemical composition on basic engineering properties of inorganic polymeric binder based on natural pozzolan, Ceramics-Silikaty, 53(3), 195-204.
Kani, E.N., Allahverdi, A., Provis, J.L. (2012). Efflorescence control in geopolymer binders based on natural pozzolan, Cement and Concrete Composites, 34(1), 25-33.
Leung, C.K., Pheeraphan, T. (1995). Very high early strength of microwave cured concrete, Cement and Concrete Research, 25(1), 136-146.
Li, Q., Sun, Z., Tao, D., Xu, Y., Li, P., Cui, H., Zhai, J. (2013). Immobilization of simulated radionuclide 133Cs+ by fly ash-based geopolymer, Journal of Hazardous Materials, 262, 325-331.
Lloyd, R.R., Provis, J.L., Van Deventer, J.S. (2010). Pore solution composition and alkali diffusion in inorganic polymer cement, Cement and Concrete Research, 40(9), 1386-1392.
Manz, O.E. (1999). Coal fly ash: a retrospective and future look, Fuel, 78(2), 133-136.
Memon, F.A., Nuruddin, M.F., Demie, S., Shafiq, N. (2011). Effect of curing conditions on strength of fly ash-based self-compacting geopolymer concrete, International Journal of Civil and Environmental Engineering, 5(8), 342-345.
Naik, T.R. (2008). Sustainability of concrete construction, Practice Periodical on Structural Design and Construction, 13(2), 98-103.
Naik, T.R., Kraus, R.N. (1999). The role of flowable slurry in sustainable developments in civil engineering, Materials and Construction: Exploring the Connection, ASCE, 826-834.
Nazari, A., Khalaj, G., Riahi, S. (2013). Retracted Aricle: ANFIS-based prediction of the compressive strength of geopolymers with seeded fly ash and rice husk-bark ash, Neural Computing and Applications, 22(3), 689-701.
Neupane, G., Donahoe, R.J. (2013). Leachability of elements in alkaline and acidic coal fly ash samples during batch and column leaching tests, Fuel, 104, 758-770.
Neupane, K. (2016). Fly ash and GGBFS based powder-activated geopolymer binders: a viable sustainable alternative of portland cement in concrete industry, Mechanics of Materials, 103, 110-122.
Nomura, Y., Fujiwara, K., Terada, A., Nakai, S., Hosomi, M. (2010). Prevention of lead leaching from fly ashes by mechanochemical treatment, Waste Management, 30(7), 1290-1295.
Nurruddin, M.F., Sani, H., Mohammed, B.S., Shaaban, I. (2018). Methods of curing geopolymer concrete: a review, International Journal of Advanced and Applied Sciences, 5(1), 31-36.
Ouellet-Plamondon, C., Habert, G. (2015). Life cycle assessment(LCA) of alkali-activated cements and concretes, Handbook of Alkali-Activated Cements, Mortars and Concretes, Woodhead Publishing, 663-686.
Palomo, A., Grutzeck, M.W., Blanco, M.T. (1999). Alkali-activated fly ashes: a cement for the future, Cement and Concrete Research, 29(8), 1323-1329.
Panagiotopoulou, C., Kontori, E., Perraki, T., Kakali, G. (2007). Dissolution of aluminosilicate minerals and by-products in alkaline media, Journal of Materials Science, 42(9), 2967-2973.
Patankar, S.V., Ghugal, Y.M., Jamkar, S.S. (2014). Effect of concentration of sodium hydroxide and degree of heat curing on fly ash-based geopolymer mortar, Indian Journal of Materials Science, 2014.
Purbasari, A., Samadhi, T.W., Bindar, Y. (2018). The effect of alkaline activator types on strength and microstructural properties of geopolymer from co-combustion residuals of bamboo and kaolin, Indonesian Journal of Chemistry, 18(3), 397-402.
Rashad, A.M., Zeedan, S.R. (2011). The effect of activator concentration on the residual strength of alkali-activated fly ash pastes subjected to thermal load, Construction and Building Materials, 25(7), 3098-3107.
Sasui, S., Kim, G., Nam, J., van Riessen, A., Hadzima-Nyarko, M. (2021). Effects of waste glass as a sand replacement on the strength and durability of fly ash/GGBS based alkali activated mortar, Ceramics International.
Satpute Manesh, B., Wakchaure Madhukar, R., Patankar Subhash, V. (2012). Effect of duration and temperature of curing on compressive strength of geopolymer concrete, Int. J. Eng. Innov. Technol, 1(5), 152-155.
Schmucker, M., MacKenzie, K.J. (2005). Microstructure of sodium polysialate siloxo geopolymer, Ceramics International, 31(3), 433-437.
Skvara, F., Kopecky, L., Nemecek, J., Bittnar, Z.D.E.N.I.K. (2006). Microstructure of geopolymer materials based on fly ash, Ceramics-Silikaty, 50(4), 208-215.
Somna, K., Jaturapitakkul, C., Kajitvichyanukul, P., Chindaprasirt, P. (2011). NaOH-activated ground fly ash geopolymer cured at ambient temperature, Fuel, 90(6), 2118-2124.
Sukmak, P., De Silva, P., Horpibulsuk, S., Chindaprasirt, P. (2015). Sulfate resistance of clay-portland cement and clay high-calcium fly ash geopolymer, Journal of Materials in Civil Engineering, 27(5), 04014158.
Xu, H., Van Deventer, J.S.J. (2000). The geopolymerisation of alumino-silicate minerals, International Journal of Mineral Processing, 59(3), 247-266.
Yahya, Z., Abdullah, M.M.A.B., Hussin, K., Ismail, K.N., Razak, R.A., Sandu, A.V. (2015). Effect of solids-to-liquids, Na 2 SiO 3 -to-NaOH and curing temperature on the palm oil boiler ash(Si+ Ca) geopolymerisation system, Materials, 8(5), 2227-2242.
Yang, T., Yao, X., Zhang, Z. (2014). Geopolymer prepared with high-magnesium nickel slag: characterization of properties and microstructure, Construction and Building Materials, 59, 188-194.
Yang, T., Yao, X., Zhang, Z., Wang, H. (2012). Mechanical property and structure of alkali-activated fly ash and slag blends, Journal of Sustainable Cement-Based Materials, 1(4), 167-178.
Yip, C.K., Lukey, G.C., Van Deventer, J.S. (2005). The coexistence of geopolymeric gel and calcium silicate hydrate at the early stage of alkaline activation, Cement and Concrete Research, 35(9), 1688-1697.
Zhang, M., El-Korchi, T., Zhang, G., Liang, J., Tao, M. (2014). Synthesis factors affecting mechanical properties, microstructure, and chemical composition of red mud-fly ash based geopolymers, Fuel, 134, 315-325.
Zhang, Z.H., Zhu, H.J., Zhou, C.H., Wang, H. (2016). Geopolymer from kaolin in China: an overview, Applied Clay Science, 119, 31-41.
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
오픈액세스 학술지에 출판된 논문
※ AI-Helper는 부적절한 답변을 할 수 있습니다.