[논문]3D 프린팅용 광 중합 수지의 두께에 따른 수축 비교

김동연; 김재홍

doi:10.14347/jtd.2021.43.1.1

3D 프린팅용 광 중합 수지의 두께에 따른 수축 비교
Comparison of shrinkage according to thickness of photopolymerization resin for 3D printing 원문보기

Journal of technologic dentistry : JTD, v.43 no.1, 2021년, pp.1 - 5

김동연 (폴드 치과기공소) , 김재홍 (부산가톨릭대학교 보건과학대학 치기공학과)

Abstract ▼ AI-Helper

Purpose: To perform a comparative study on curing shrinkage according to the thickness of photopolymerization resin. Methods: Stainless steel molds of 2, 4, and 6 mm heights were prepared. The 2, 4, and 6 mm-height molds were classified as the 2H, 4H, and 6H groups, respectively. A photopolymerization resin was injected into the stainless steel mold. Photopolymerization was carried out using a photopolymer machine. During photopolymerization, the wavelength and intensity of 400~405 nm were set to 10, the highest intensity among 1~10. Photopolymerization was performed for 30 min per specimen (each group=10). The inner and outer areas of the specimen were measured. The data were analyzed using one-way ANOVA and Kruskal-Wallis H test (α=0.05). Results: In terms of the inner and outer diameters of the photopolymerization resin specimen, the 2H group contracted the most, whereas the 6H group contracted the least. A statistically significant difference was found between the groups (p<0.05). Conclusion: The amount of light irradiation of the photopolymerization resin must be adjusted according to the thickness.

주제어

AI 본문요약
AI-Helper

* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.

문제 정의

치과 보철물은 형태가 다양하고 두께도 다르기 때문에 광 조사에 따른 수축 연구가 필요한 상황이다. 따라서 본 연구에서는 광 중합 수지의 다양한 두께에 따른 경화 수축을 비교 분석하고자 한다.
본 연구에서는 광 경화 수지의 시편 두께에 따른 경화 수축을 분석하여 다음과 같이 결론을 얻었다. 광 경화 수지의 시편의 두께에 따라서 경화 수축이 상이하게 나타났다.
맞춤식 제작은 환자 마다 수복물의 형태가 다르고 이에 따른 두께도 다양하다. 이에 본 연구에서는 수복물의 두께를 고려하여 광 중합 수지를 사용하여 2 mm, 4 mm, 6 mm의 기준으로 제작하였을 경우 수축에 대해서 평가해 보고자 하였다.

제안 방법

)로 설정하였다. 광 중합 수지 경화가 완료된 시편은 디지털 측정기구(C₂₂0; Kroeplin, Schlüchtern, Germany)를 사용하여 시편의 내측(inner) 및 외측(outer)부위를 선형 측정(X₂)하였다(Fig. 4) [6]. 측정 계산법은 ASTM C 326 세라믹 선형측정 계산법을 참고하였다[16].
광 중합기(Cure Box-320; Denstar, Daegu, Korea)를 사용 하 여광 중합을 진행하였다. 광 중합 사용 시 400~405 nm의 파장과 광도의 설정은 1~10단계 중 가장 높은 강도인 10단계로 설정하였다.
스테인리스강 몰드 원형 내벽에 바세린을 도포하여 광 중합 후 분리 될 수 있도록 하였다[6]. 스테인리스강 바닥 부분에 스카치 테이프 (#550 Scotch; 3M, Saint Paul, MN, USA)를 부착하여 광 중합 수지가 누출되지 않도록 방지하였다[6].
스테인리스강 바닥 부분에 스카치 테이프 (#550 Scotch; 3M, Saint Paul, MN, USA)를 부착하여 광 중합 수지가 누출되지 않도록 방지하였다[6]. 스테인리스강 몰드 원형 내부에 광중합 수지(NextDent C&B; NextDent, Soesterberg, Netherlands) 를 주입하였다. 여분의 광 중합 수지는 디스크를 사용하여 제거하였으며, 몰드의 높이와 광 중합 수지의 높이를 일치하도록 하였다[6].
광 중합 사용 시 400~405 nm의 파장과 광도의 설정은 1~10단계 중 가장 높은 강도인 10단계로 설정하였다. 시편당 30분씩 광 중합을 진행하였다. 세 집단 모두 동일하게 반복 진행하였으며, 각각 그룹 마다 10개의 시편을 제작하여 총 30개의 시편을 제작하였다(Fig.
스테인리스강 몰드 원형 내부에 광중합 수지(NextDent C&B; NextDent, Soesterberg, Netherlands) 를 주입하였다. 여분의 광 중합 수지는 디스크를 사용하여 제거하였으며, 몰드의 높이와 광 중합 수지의 높이를 일치하도록 하였다[6].
치과 분야에서는 3D 프린팅용 광 중합 수지를 사용하여 수복물을 제작한다. 특히 구강 내 환경을 인기한 모형(model), 임시 단관(temporary crown), 임시 교의치(temporary bridge), 주조용 코핑(casting coping)등 맞춤식 제작을 한다. 맞춤식 제작은 환자 마다 수복물의 형태가 다르고 이에 따른 두께도 다양하다.

대상 데이터

중합을 진행하였다. 광 중합 사용 시 400~405 nm의 파장과 광도의 설정은 1~10단계 중 가장 높은 강도인 10단계로 설정하였다. 시편당 30분씩 광 중합을 진행하였다.
본 연구에서 2 mm, 4 mm, 6 mm의 스테인리스강 몰드를 선정하게 된 근거는 다음과 같다. 실험에 사용한 광 중합 수지는 임시 인레이, 임시 단관, 임시 교의치용으로 제공되고 있으나 수복물의 두께에 대한 수축 연구는 미비하였다.
본 연구의 시편을 제작하기 위해서 ISO 4049를 참고하였고, 시편의 두께는 2 mm, 4 mm, 6 mm 의 두께로 스테인리스강 몰드를 준비하였다(Fig. 1, 2) [14, 15]. 집단은 세 집단으로 다음과 같이 분류하였다.
시편당 30분씩 광 중합을 진행하였다. 세 집단 모두 동일하게 반복 진행하였으며, 각각 그룹 마다 10개의 시편을 제작하여 총 30개의 시편을 제작하였다(Fig. 3).

데이터처리

dAnalysed by one-way ANOVA.
0; IBM, Armonk, NY, USA)을 사용하였으며, 정규성 검증인 Kolmogorov–Smirnov를수행하였다. 시편 내측에서는 정규성 검증을 충족하여 ANOVA를 실시하였으며 사후 검증은 Duncan으로 분석하였다(α=0.05). 시편 외부에서는 정규성을 충족하지 못하여 비모수 검증인 Kruskal–Wallis 검정을 실시하였으며 사후 검정은 Mann–Whitney로 분석하고 Bonferroni correction으로 보정하였다(0.
05). 시편 외부에서는 정규성을 충족하지 못하여 비모수 검증인 Kruskal–Wallis 검정을 실시하였으며 사후 검정은 Mann–Whitney로 분석하고 Bonferroni correction으로 보정하였다(0.05/3=0.017).
측정된 데이터는 통계프로그램(IBM SPSS 22.0; IBM, Armonk, NY, USA)을 사용하였으며, 정규성 검증인 Kolmogorov–Smirnov를수행하였다. 시편 내측에서는 정규성 검증을 충족하여 ANOVA를 실시하였으며 사후 검증은 Duncan으로 분석하였다(α=0.

이론/모형

4) [6]. 측정 계산법은 ASTM C 326 세라믹 선형측정 계산법을 참고하였다[16].

성능/효과

가장 많이 수축한 집단은 2H 집단의 10.1%이며, 가장 적게 수축한 집단은 6H 집단의 3.5%로 나타났다. 집단간 통계적으로도 유의한 차이를 보였다(p<0.

후속연구

증가하게 된다고 보고된 바 있다[22]. 이러한 문제를 해결하기 위해서 첨가제를 첨가하여 수축 현상을 최소화하려는 연구들이 존재하나, 본 연구의 실험결과를 통해 치과 보철물 제작 시 부피에 따라서 광조사량을 조절하여 가교밀도를 조절하는 것도 필요하다고 판단된다. 특히 본 실험은 광 경화기에서 광 세기가 조절이 가능함으로써 임상가 (치과의사, 치과기공사, 치과위생사)에게 기초적인 자료를 제공하는 것이 필요할 것으로 생각된다.
그러나 시편에 동일한 광 조사량을 통제하고자 10단계에서만 광 조사를 하고자 노력하였다. 추후 연구에서는 광 경화 수지의 부피에 따라서 광 조사량을 분석하는 것이 필요하며, 물성평가를 추가로 평가하여 최적의 조건인 광 경화 조건을 찾는 것이 중요할 것이다.
이러한 문제를 해결하기 위해서 첨가제를 첨가하여 수축 현상을 최소화하려는 연구들이 존재하나, 본 연구의 실험결과를 통해 치과 보철물 제작 시 부피에 따라서 광조사량을 조절하여 가교밀도를 조절하는 것도 필요하다고 판단된다. 특히 본 실험은 광 경화기에서 광 세기가 조절이 가능함으로써 임상가 (치과의사, 치과기공사, 치과위생사)에게 기초적인 자료를 제공하는 것이 필요할 것으로 생각된다.
또한 Kim [6]에 의하면 광 중합 수지는 광 조사 시간이 길어질수록 수축에 영향을 미친다고 보고한 바 있다. 한편 3D 프린팅을 사용한 치과 보철물은 광 조사에 의해서 형태 및 두께가 다양하게 제작되고 있으며, 추가로 광 조사를 진행하여 최종 경화 과정을 거친다. 치과 보철물은 형태가 다양하고 두께도 다르기 때문에 광 조사에 따른 수축 연구가 필요한 상황이다.

참고문헌 (22)

Kim DY, Kim JH, Lee BI, Lee JH, Kim WS, Park JY. Accuracy evaluation of dental model scanner according to occlusal attrition type. J Tech Dent. 2020;42:313-320.

원문보기 상세보기
Kim DY, Kim JH, Kim HY, Kim WC. Comparison and evaluation of marginal and internal gaps in cobalt-chromium alloy copings fabricated using subtractive and additive manufacturing. J Prosthodont Res. 2018;62:56-64.

상세보기
van Noort R. The future of dental devices is digital. Dent Mater. 2012;28:3-12.

상세보기
Azari A, Nikzad S. The evolution of rapid prototyping in dentistry: a review. Rapid Prototyp J. 2009;15:216-225.

상세보기
Lee BI, You SG, You SM, Kim JH. Comparison of three-dimensional adaptation as per the rinsing time of temporary crown manufactured using a digital light processing printer. J Tech Dent. 2020;42:334-340.

원문보기 상세보기
Kim DY. Difference between shrinkage rate of irradiation amount of 3D printing UV curable resin and shrinkage rate according to a constant temperature water bath. J Korean Acad Dent Technol. 2020;42:113-120.

원문보기 상세보기
Sa MW, Kim JY. Comparison analysis and fabrication of Hollow Shaft scaffolds using polymer deposition system. Tissue Eng Regen Med. 2015;12:46-52.

상세보기
Park YD, Kang W. Comparative analysis of the flexural strength of provisional restorative resins using a digital light processing printer according to the post-curing method. J Tech Dent. 2020;42:341-347.

원문보기 상세보기
Prpic V, Slacanin I, Schauperl Z, Catic A, Dulcic N, Cimic S. A study of the flexural strength and surface hardness of different materials and technologies for occlusal device fabrication. J Prosthet Dent. 2019;121:955-959.

상세보기
Park DR, Son J. Comparison between mechanical properties and biocompatibility of experimental 3D printing denture resins according to photoinitiators. J Tech Dent. 2020;42:355-361.

원문보기 상세보기
Kim JH, Kim KB. Analysis of the quality of dental prostheses printed by digital light-processing technology. J Tech Dent. 2020;42:197-201.

원문보기 상세보기
Kang SY, Lee HN, Kim EB, Lee KE, Kim JH, Kim WC. Fitness of heat - pressed ceramic laminate veneer using additive manufacturing process: 3 dimensional analysis. J Korean Acad Dent Technol. 2017;39:137-143.
Kim DY, Jeon JH, Kim JH, Kim HY, Kim WC. Reproducibility of different arrangement of resin copings by dental microstereolithography: evaluating the marginal discrepancy of resin copings. J Prosthet Dent. 2017;117:260-265.

상세보기
International Organization for Standardization. Dentistry - polymer-based filling, restorative and luting materials. 3rd ed. Geneva: International Organization for Standardization; 2000.
Bae S, Lee J, Ra J. Evaluation of the changes in polymerization of TheraCal LC with various light-curing time and distance. J Korean Acad Pediatr Dent. 2019;46:392-399.
ASTM International. ASTM C326-09 (2018), standard test method for drying and firing shrinkages of ceramic whiteware clays. West Conshohocken (PA): ASTM International; 2009.
Do HS, Kim DJ, Kim HJ. Application of UV-curable materials. JAI. 2003;4:41-51.
Jassim ZM, Majeed MA. Comparative evaluation of the fracture strength of monolithic crowns fabricated from different all-ceramic CAD/CAM materials (an in vitro study). Biomed Pharmacol J. 2018;11:1689-1697.

상세보기
Spear F, Holloway J. Which all-ceramic system is optimal for anterior esthetics? J Am Dent Assoc. 2008;139 Suppl: 19S-24S.

상세보기
Karalekas D, Aggelopoulos A. Study of shrinkage strains in a stereolithography cured acrylic photopolymer resin. J Mater Process Technol. 2003;136:146-150.

상세보기
Park JH, Choi NS. Polymerization shrinkage distribution of a dental composite during dental restoration observed by digital image correlation method. Compos Res. 2017;30:393-398.

원문보기 상세보기
Kwon Y, Cho UR. Study on the improvement of film shrinkage in UV-curing process. Polymer(Korea). 2011;35:320-324.

표제어: PCR

동의어: Packet Collision Rate

용어 설명 출처 목록 (6)

용어 설명: PCR은 세균 특이성이 있는 primer를 이용하여 적은 수의 세균이 있을지라도 쉽게 검출할 수 있는 유용한 방법이며, 이를 이용하여 구강 내 치면세균막이나 타액에서 직접 세균을 검출할 수 있게 되었다[8].

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증