[논문]Mechanical behaviour of mullite composites reinforced with mullite fibres

Ha, J.-S.; Chawla, K.K.

doi:10.1016/0921-5093(95)09874-7

Mechanical behaviour of mullite composites reinforced with mullite fibres

Materials science & engineering. properties, microstructure and processing. A, Structural materials, v.203 no.1/2, 1995년, pp.171 - 176

Ha, J.-S. (Department of Materials Engineering, Andong National University, 388 Songchun-Dong, Andong 760-749, South Korea) , Chawla, K.K. (Department of Materials and Metallurgical Engineering, New Mexico Institute of Mining and Technology, Socorro, NM 87801, USA)

Abstract ▼ AI-Helper

AbstractMullite matrix composites uniaxially reinforced with uncoated and BN (0.3 or 1 μm thick) coated mullite fibres were consolidated to 82 to 98% of TD (theoretical density) at 1300 °C by using a colloidal processing route to make mullite matrix. The mechanical properties were characterized by flexural testing and chevron-notch tests for fracture toughness measurement. The samples with uncoated and 0.3 μm BN-coated fibres failed in a brittle manner without any toughening effect of the fibres. In contrast, the sample with 1 μm BN-coated fibres showed toughened composite behaviour (i.e. load-carrying capacity following maximum load) with a significant enhancement in toughness (e.g. about 12 MPa m12 in the as-fabricated state), despite a relatively low density of about 90% TD. The room temperature ultimate strength (320 MPa) and fracture toughness of this composite decreased a little by heat treatment at 1320 °C for inducing complete transformation to mullite of the matrix, probably due to the degradation of fibre strength.

주제어

참고문헌 (19)

Singh 8 636 1987
Yeheskel 9 687 1988
NASA HITEMP Review Norkitis 61 1991
Norkitis 1992 presented at the 94th Annual Meeting of the American Ceramic Society SnO2 interfacial coatings for sapphire-reinforced alumina composites
NASA HITEMP Review Jaskowiak 60 1991
Mater. Sci. Eng. Ha A161 303 1993 10.1016/0921-5093(93)90525-J

상세보기
J. Mater. Sci. Lett. Ha 12 84 1993 10.1007/BF00241855

상세보기
Ceram. Int. Ha 19 299 1993 10.1016/0272-8842(93)90042-P

상세보기
Bubsey 753 1979 Ceramics for High Performance Applications III: Reliability
Wu 176 1984 Chevron-Notched Specimens: Testing and Stress Analysis
Int. J. Fracture Wu 26 R43 1984 10.1007/BF01157552

상세보기
J. Am. Ceram. Soc. Singh 73 2930 1990 10.1111/j.1151-2916.1990.tb06697.x

상세보기
Acta Metall. Evans 37 2567 1989 10.1016/0001-6160(89)90291-5

상세보기
J. Am. Ceram. Soc. Evans 73 187 1990 10.1111/j.1151-2916.1990.tb06493.x

상세보기
J. Mech. Phys. Solids Budiansky 34 167 1986 10.1016/0022-5096(86)90035-9

상세보기
J. Am. Ceram. Soc. Marshall 68 225 1985 10.1111/j.1151-2916.1985.tb15313.x

상세보기
Composites Davidge 18 92 1987 10.1016/0010-4361(87)90487-3

상세보기
Acta Metall. Sutcu 37 651 1989 10.1016/0001-6160(89)90249-6

상세보기
J. Am. Ceram. Soc. Hirata 74 2438 1991 10.1111/j.1151-2916.1991.tb06781.x

상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Mechanical behaviour of mullite composites reinforced with mullite fibres

Abstract ▼ AI-Helper

주제어

참고문헌 (19)

이 논문을 인용한 문헌

관련 콘텐츠

원문 URL 링크

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트