[논문]Characterization of Ag and Au nanoparticles created by nanosecond pulsed laser ablation in double distilled water

Nikolov, A.S.; Nedyalkov, N.N.; Nikov, R.G.; Atanasov, P.A.; Alexandrov, M.T.

doi:10.1016/j.apsusc.2010.10.146

Characterization of Ag and Au nanoparticles created by nanosecond pulsed laser ablation in double distilled water

Applied surface science, v.257 no.12, 2011년, pp.5278 - 5282

Nikolov, A.S. (Institute of Electronics, Bulgarian Academy of Sciences, Tzarigradsko shousse 72, Sofia 1784, Bulgaria) , Nedyalkov, N.N. , Nikov, R.G. , Atanasov, P.A. , Alexandrov, M.T.

Abstract ▼ AI-Helper

Pulsed laser ablation of Ag and Au targets, immersed in double-distilled water is used to synthesize metallic nanoparticles (NPs). The targets are irradiated for 20min by laser pulses at different wavelengths-the fundamental and the second harmonic (SHG) (λ=1064 and 532nm, respectively) of a Nd:YAG laser system. The ablation process is performed at a repetition rate of 10Hz and with pulse duration of 15ns. Two boundary values of the laser fluence for each wavelength under the experimental conditions chosen were used-it varied from several J/cm2 to tens of J/cm2. Only as-prepared samples were measured not later than two hours after fabrication. The NPs shape and size distribution were evaluated from transmission electron microscopy (TEM) images. The suspensions obtained were investigated by optical transmission spectroscopy in the near UV and in the visible region in order to get information about these parameters. Spherical shape of the NPs at the low laser fluence and appearance of aggregation and building of nanowires at the SHG and high laser fluence was seen. Dependence of the mean particle size at the SHG on the laser fluence was established. Comments on the results obtained have been also presented.

주제어

참고문헌 (15)

Mater. Chem. Phys. Mallick 97 283 2006 10.1016/j.matchemphys.2005.08.011

상세보기
Nat. Mater. Ohko 2 29 2003 10.1038/nmat796

상세보기
J. Am. Chem. Soc. Liu 130 9 2780 2008 10.1021/ja711298b

상세보기
Polymer Murali Mohan 48 158 2007 10.1016/j.polymer.2006.10.045

상세보기
Chem. Mater. Corbierre 18 11 2628 2006 10.1021/cm060235v

상세보기
Science Yin 304 711 2004 10.1126/science.1096566

상세보기
J. Phys. Chem. B Link 103 40 8410 1999 10.1021/jp9917648

상세보기
Nano Today Jain 2 2 18 2007 10.1016/S1748-0132(07)70016-6

상세보기
Science Bell 299 1688 2003 10.1126/science.1083671

상세보기
J. Nanopart. Res. Khaydarov 11 1193 2009 10.1007/s11051-008-9513-x

상세보기
Langmuir Huang 12 4 909 1996 10.1021/la950435d

상세보기
Rev. Adv. Mater. Sci. Tien 18 750 2008
Laser Phys. Lett. Hajiesmaeilbaigi 3 5 252 2006 10.1002/lapl.200510082

상세보기
Appl. Phys. A Tilaki 84 215 2006 10.1007/s00339-006-3604-2

상세보기
Appl. Phys. A Simakin 79 1127 2004 10.1007/s00339-004-2660-8

상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Characterization of Ag and Au nanoparticles created by nanosecond pulsed laser ablation in double distilled water

Abstract ▼ AI-Helper

주제어

참고문헌 (15)

이 논문을 인용한 문헌

관련 콘텐츠

연관된 기능

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트