In this study, with a view to improve the mechanical properties, the influence of the change in the micro-structure, crystal phase and mechanical properties were evaluated, by changing the amount of one of the sintering additives, Al2O3 and the HIP sintering conditions, from the viewpoint of the mic...
In this study, with a view to improve the mechanical properties, the influence of the change in the micro-structure, crystal phase and mechanical properties were evaluated, by changing the amount of one of the sintering additives, Al2O3 and the HIP sintering conditions, from the viewpoint of the micro-structure consisting of α-Si3N4, β-Si3N4 and glassy grain boundary phase. The experimental results showed that 1) the combination of the sintering additives makes a various sorts of crystals and glassy phase formed which promotes the densification, 2) the addition of Al2O3 was effective in the densification, further, 3) as for the HIP sintering condition, N2 gas pressure higher than 60MPa greatly influences the transformation from α-Si3N4 to β-Si3N4 with densification.Finally, Si3N4 ceramics consist of both α-Si3N4 and β-Si3N4 crystal phase has been applied for various industrial wear parts, for example, cutting tool, crasher parts, bonding tool for FPD and semiconductor with heating, etc. In these applications, it was recognized that this materials shows the excellent performance comparing with conventional materials.
In this study, with a view to improve the mechanical properties, the influence of the change in the micro-structure, crystal phase and mechanical properties were evaluated, by changing the amount of one of the sintering additives, Al2O3 and the HIP sintering conditions, from the viewpoint of the micro-structure consisting of α-Si3N4, β-Si3N4 and glassy grain boundary phase. The experimental results showed that 1) the combination of the sintering additives makes a various sorts of crystals and glassy phase formed which promotes the densification, 2) the addition of Al2O3 was effective in the densification, further, 3) as for the HIP sintering condition, N2 gas pressure higher than 60MPa greatly influences the transformation from α-Si3N4 to β-Si3N4 with densification.Finally, Si3N4 ceramics consist of both α-Si3N4 and β-Si3N4 crystal phase has been applied for various industrial wear parts, for example, cutting tool, crasher parts, bonding tool for FPD and semiconductor with heating, etc. In these applications, it was recognized that this materials shows the excellent performance comparing with conventional materials.
4) M. Nagano, H. Sano, S. Sakaguchi, G. B. Zheng, and Y. Uchiyama: "The Effect of Oxygen Introduction on Oxidation Resistance and Cutting Performance of Silicon Nitride Ceramics", Materials Science Forum, Vols., (2006) 534-536.
5) Y. Hasegawa, H. Tanaka, M. Tsutsumi, and H. Suzuki: "Oxidation Behavior of Hot-Pressed Si 3 N 4 with Addition of Y 2 O 3 and Al 2 O 3 ", Yogyo-Kyokai-Shi, 88 (1980) 72-97.
0388-0664 17 2 1984
0914-5400 PEZZOTTI G 104 3 226 1996 10.2109/jcersj.104.226
※ AI-Helper는 부적절한 답변을 할 수 있습니다.