[논문]Ta/NiFe/FeMn thin films with enhanced exchange bias prepared at room temperature by rotational deposition

Yuan, F.T.; Tsai, C.Y.; Hsu, J.H.; Lin, K.F.; Mei, J.K.

doi:10.1016/j.tsf.2013.04.015

Ta/NiFe/FeMn thin films with enhanced exchange bias prepared at room temperature by rotational deposition

Thin solid films, v.536, 2013년, pp.244 - 248

Yuan, F.T. , Tsai, C.Y. , Hsu, J.H. , Lin, K.F. , Mei, J.K.

Abstract ▼ AI-Helper

Ta(20nm)/NiFe(5nm)/FeMn(20nm) films were deposited on glass substrates by rotational deposition at room temperature. A significant enhancement in the exchange bias field (Heb) associated with very low coercivity (Hc) was achieved for the samples prepared at rotational speed (Rrpm) of 1rpm. The Heb and Hc of the samples with Rrpm=1rpm were approximately double and smaller than half of those deposited by conventional continuous sputtering, respectively. Structural studies reveal that the rotational deposition not only improves the crystallization of FeMn but also facilitates the development of (111) texture through a preferred Ta(200) orientation. The sputtering powers of the constituent layers: WTa, WNiFe and WFeMn significantly affected the magnetic properties. Remarkable exchange bias properties, such as Heb of 26.67kA/m and Hc of 1.99kA/m were achieved at Rrpm=1rpm, WTa=40W, WNiFe=70W and WFeMn=140W. The Heb value obtained with the Ta/NiFe/FeMn films is comparable to that with the commercialized NiFe/IrMn system with a similar layered structure and it is more than 3 times larger than that of the sample deposited with fixed substrate in this study. The intensity of the FeMn(111) peak and the Scherrer coherent length are proportional to the Heb, indicating that the exchange bias behavior of the sample was dominated by the stability of the antiferromagnetic spin structure. The rotational deposition method proposed in this study favors practical applications in terms of both production cost and performance of spintronic devices.

주제어

참고문헌 (46)

Phys. Rev. Meiklejohn 102 1413 1956 10.1103/PhysRev.102.1413

상세보기
Phys. Rev. B Stiles 60 12950 1999 10.1103/PhysRevB.60.12950

상세보기
Phys. Rev. Hou 63 024411 2000 10.1103/PhysRevB.63.024411

상세보기
Eur. Phys. J. B Hu 40 265 2004 10.1140/epjb/e2004-00272-0

상세보기
Phys. Rev. B Binek 72 054408 2005 10.1103/PhysRevB.72.054408

상세보기
Solid State Commun. Makhlouf 145 1 2008 10.1016/j.ssc.2007.10.019

상세보기
Phys. Rev. Lett. Liu 91 037207 2003 10.1103/PhysRevLett.91.037207

상세보기
J. Magn. Magn. Mater. Nogues 192 203 1999 10.1016/S0304-8853(98)00266-2

상세보기
Phys. Rev. B Xi 61 80 2000 10.1103/PhysRevB.61.80

상세보기
J. Appl. Phys. Hu 92 1009 2002 10.1063/1.1486020

상세보기
Phys. Rev. B Leighton 65 064403 2002 10.1103/PhysRevB.65.064403

상세보기
J. Appl. Phys. van der Zaag 79 5103 1996 10.1063/1.361315

상세보기
J. Appl. Phys. Hu 94 2529 2003 10.1063/1.1594271

상세보기
Phys. Rev. B Zhang 65 054406 2001 10.1103/PhysRevB.65.054406

상세보기
J. Appl. Phys. Pakala 87 6653 2000 10.1063/1.372800

상세보기
IEEE Trans. Magn. Pakala 36 2620 2000 10.1109/20.908535

상세보기
J. Appl. Phys. Krishnan 83 6810 1998 10.1063/1.367815

상세보기
J. Appl. Phys. Han 81 340 1997 10.1063/1.364116

상세보기
J. Magn. Magn. Mater. Nakatani 173 321 1997 10.1016/S0304-8853(97)00201-1

상세보기
J. Appl. Phys. Park 79 6228 1996 10.1063/1.361891

상세보기
IEEE Trans. Magn. Wang 32 4660 1996 10.1109/20.539110

상세보기
J. Appl. Phys. Wong 79 7896 1996 10.1063/1.362401

상세보기
IEEE Trans. Magn. Kanak 44 238 2008 10.1109/TMAG.2007.909438

상세보기
J. Appl. Phys. Bae 87 6650 2000 10.1063/1.372799

상세보기
Appl. Phys. Lett. Kiwi 75 3995 1999 10.1063/1.125517

상세보기
J. Appl. Phys. Tsang 52 2471 1981 10.1063/1.328970

상세보기
J. Magn. Magn. Mater. Schlenker 54-57 801 1986 10.1016/0304-8853(86)90260-X

상세보기
J. Appl. Phys. Liu 87 6644 2000 10.1063/1.372797

상세보기
Phys. Rev. Lett. Ouyang 98 097204 2007 10.1103/PhysRevLett.98.097204

상세보기
Phys. Rev. B Del Bianco 70 052401 2004 10.1103/PhysRevB.70.052401

상세보기
Appl. Phys. Lett. Miltenyi 75 2304 1999 10.1063/1.124998

상세보기
J. Appl. Phys. Moran 79 5109 1996 10.1063/1.361317

상세보기
J. Appl. Phys. Tang 100 023914 2006 10.1063/1.2219698

상세보기
J. Magn. Magn. Mater. Kagerer 217 139 2000 10.1016/S0304-8853(00)00315-2

상세보기
J. Appl. Phys. Hu 102 113911 2007 10.1063/1.2821357

상세보기
IEEE Trans. Magn. Choukh 33 3676 1997 10.1109/20.619535

상세보기
Appl. Phys. Lett. Mewes 76 1057 2000 10.1063/1.125937

상세보기
Phys. Rev. B Mougin 63 060409R 2001 10.1103/PhysRevB.63.060409

상세보기
J. Appl. Phys. Morales 93 4729 2003 10.1063/1.1560859

상세보기
IEEE Trans. Magn. Nishioka 32 3949 1995 10.1109/20.489826

상세보기
J. Appl. Phys. Fujiwara 79 6286 1996 10.1063/1.362039

상세보기
IEEE Trans. Magn. Nakatani 33 3682 1997 10.1109/20.619537

상세보기
J. Appl. Phys. Sankaranarayanan 96 7428 2004 10.1063/1.1815048

상세보기
Cullity 170 2001 Elements of X-ray Diffraction
IEEE Trans. Magn. Aley 44 2820 2008 10.1109/TMAG.2008.2001317

상세보기
J. Phys. D: Appl. Phys. King 34 528 2001 10.1088/0022-3727/34/4/315

상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Ta/NiFe/FeMn thin films with enhanced exchange bias prepared at room temperature by rotational deposition

Abstract ▼ AI-Helper

주제어

참고문헌 (46)

이 논문을 인용한 문헌

관련 콘텐츠

원문 URL 링크

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트