NTIS 바로가기Engineering fracture mechanics, v.108, 2013년, pp.50 - 64
Kim, I. , Zhao, Y. , Choi, B.H. , Lee, J.M. , Lee, K.S. , Lee, J.M.
The effects of various misalignments of circular notched bar (CNB) specimens on the fatigue crack propagation behavior of pipe grade polyethylene were investigated by finite element analyses. Generally, as the misalignments increased, the asymmetric crack growth accelerated with a consequent decreas...
J Mater Sci Lu 26 917 1991 10.1007/BF00576768 Discontinuous crack growth in polyethylene under a constant load
Chudnovsky A. Crack layer theory, NASA, Report #174634; 1984.
Polym Engng Sci Choi 49 1421 2009 10.1002/pen.21436 The use of crack layer theory to predict the lifetime of the fatigue crack growth of high density polyethylene
Polymer Chan 24 234 1983 10.1016/0032-3861(83)90139-8 Slow stable crack growth in high density polyethylenes
J Mater Sci Parsons 34 3315 1999 10.1023/A:1004616728535 Correlation of stepwise fatigue and creep slow crack growth in high density polyethylene
J Mater Sci Parsons 35 1857 2000 10.1023/A:1004741713514 Effect of strain rate on stepwise fatigue and creep slow crack growth in high density polyethylene
Int J Fract Jasarevic 158 73 2000 10.1007/s10704-009-9365-0 Observation and modeling of brittle fracture initiation in a micro-heterogeneous material
J Appl Phys Chudnovsky 62 4124 1987 10.1063/1.339128 A probabilistic model of brittle crack formation
Int J Press Ves Pip Lei 73 199 1997 10.1016/S0308-0161(97)00070-7 Non-linear, axi-symmetric finite element analyses of a circumferentially cracked bar specimen
Int J Press Ves Pip Nakano 44 3 1990 10.1016/0308-0161(90)90003-Z Measurement of dynamic fracture toughness by longitudinal impact of precracked round bar
Polymer Favier 43 1375 2002 10.1016/S0032-3861(01)00701-7 Slow crack propagation in polyethylene under fatigue at controlled stress intensity
Engng Fract Mech Frank 76 2780 2009 10.1016/j.engfracmech.2009.06.009 A fracture mechanics concept for the accelerated characterization of creep crack growth in PE-HD pipe grades
Polym Test Pinter 26 180 2007 10.1016/j.polymertesting.2006.09.010 Cyclic crack growth tests with CRB specimens for the evaluation of the long-term performance of PE pipe grades
Zhou 2006 Crack initiation in pipe grade polyethylene. ANTEC 2006
Engng Fract Mech Redhead 101 2 2013 10.1016/j.engfracmech.2012.09.022 Investigation of slow crack growth initiation in polyethylene pipe grades with accelerated cyclic tests
Choi 2010 Evaluation of the crack initiation characteristics of pipe grade polyethylene under fatigue loads. ANTEC 2010
Int J Fract Zhao 167 127 2011 10.1007/s10704-010-9532-3 Variation of the fatigue lifetime with the initial notch geometry of circular notched bar specimens
Engng Fract Mech Ibrahim 28 455 1987 10.1016/0013-7944(87)90190-1 Validity requirements for fracture toughness measurements from small circumferentially notched cylindrical specimens
ASME PVP Ibrahim 388 155 1999 An analytical approach for calculating KIc From eccentrically cracked cylinder specimen
Int J Press Ves Pip Rihan 83 388 2006 10.1016/j.ijpvp.2006.02.019 Circumferential notched tensile (CNT) tests for generating KIscc data for cast iron vessels used in hot caustic solutions
J Basic Engng Erdogan 85 519 1963 10.1115/1.3656897 On the crack extension in plates under plane loading and transverse shear
Int J Press Ves Pip Ha 81 401 2004 10.1016/j.ijpvp.2004.03.011 Creep crack growth properties for 12CrWCoB rotor steel using circular notched specimens
Engng Fract Mech Ibrahim 64 49 1999 10.1016/S0013-7944(99)00056-9 Eccentricity correction for the evaluation of fracture toughness from cylindrical notched test small specimens
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.