NTIS 바로가기Polymer testing, v.33, 2014년, pp.161 - 171
Frank, A. , Pinter, G.
Several tests methods are available for the characterization of the slow crack growth (SCG) resistance of polyethylene (PE) for pipe applications. Unfortunately, due to the increase of the SCG resistance of modern PE pipe grades, these test methods are exceeding practical time frames so that new tes...
Kunststoffe Richard 49 10 516 1959 Trinkwasserrohre aus Niederdruckpolyathylen
Kunststoffe Gaube 75 7 412 1985 Creep rupture strength and aging of HDPE pipes: 30 years experience in testing of pipes
Die Angewandte Makromolekulare Chemie Lang 247 15 131 1997 10.1002/apmc.1997.052470109 Applicability and limitations of current lifetime prediction models for thermoplastics pipes under internal pressure
3R International Lang 36 1 40 1997 Polymerphysikalische Ansatze zur Beschreibung des Deformations- und Versagensverhaltens von PE-Rohren
Bromstrup 2004 PE100 Pipe Systems
3R International Hessel 45 3/4 128 2006 50 years of polyethylene piping. Engineering perspective
ISO 9080 2012 Plastics Piping and Ducting Systems - Determination of the Long-term Hydrostatic Strength of Thermoplastics Materials in Pipe Form by Extrapolation
ASTM D2837-11. Standard Test Method for Obtaining Hydrostatic Design Basis for Thermoplastic Pipe Materials or Pressure Design Basis for Thermoplastic Pipe Products.
PAS 1075 2009 Rohre aus Polyethylen fur alternative Verlegetechniken
J. Mater. Sci. Barker 18 1095 1983 10.1007/BF00551979 The performance and cause of failure of polyethylene pipes subjected to constant and fluctuating internal pressure loadings
Kunststoffe Ifwarson 79 6 525 1989 Gebrauchsdauer von Polyethylenrohren unter Temperatur und Druckbelastung
Plast. Rub. Compos. Pro Brown 17 4 255 1992 The fundamental material parameters that govern slow crack growth in linear polyethylens
Kuhlman 1992 Proceedings Plastics Pipes VIII, Koenigshof, Netherlands Forecasting the long-term service performance of polyethylene gas distribution pipes
Beech 2001 Proceedings Plastic Pipes XI, Munchen, Germany Mechanisms of Slow Crack Growth in PE Pipe Grades
ISO 13479 2009 Polyolefin Pipes for the Conveyance of Fluids - Determination of Resistance to Crack Propagation - Test Method for Slow Crack Growth on Notched Pipes
ASTM F1473-11. Standard Test Method for Notch Tensile Test to Measure the Resistance to Slow Crack Growth of Polyethylene Pipes and Resins.
Plast. Rub. Compos. Pro Beech 27 418 1998 Slow crack growth performance of today's plastics pipeline materials
ISO 16241 2005 Notch Tensile Test to Measure the Resistance to Slow Crack Growth of Polyethylene Materials for Pipe and Fitting Products (PENT)
Polym. Test. Nezbedovaa 32 1 106 2013 10.1016/j.polymertesting.2012.09.009 The applicability of the Pennsylvania Notch Test for a new generation of PE pipe grades
Polym. Korea Choi 21 83 1997 Residual stresses in plastic pipes and fitting - I. Methods for experimental analysis
Kunststoffe Fleissner 77 45 1987 Langsames Risswachstum und Zeitstandfestigkeit von Rohren aus Polyethylen
Polym. Eng. Sci. Fleissner 38 330 1998 10.1002/pen.10194 Experience with a full notch creep test in determining the stress crack performance of polyethylene
ISO 16770 2004 Plastics - Determination of Environmental Stress Cracking (ESC) of Polyethylene - Full-notch Creep Test (FNCT)
Polymer Kurelec 46 17 6369 2005 10.1016/j.polymer.2005.05.061 Strain hardening modulus as a measure of environmental stress crack resistance of high density polyethylene
Polymer Deblieck 52 2979 2011 10.1016/j.polymer.2011.03.055 Failure mechanisms in polyolefins: the role of crazing, shear yielding and the entanglement network
Havermans van Beek 2010 Proceedings Pipes XV, Vancouver, Canada An elegant and fast method to predict the slow crack growth behavior of high density polyethylene pipe materials
Havermans 2012 Proceedings Plastic Pipes XVI, Barcelona, Spain Strain hardening modulus: an accurate measure for slow crack growth behavior of HDPE pipe materials
3R International Lang 44 1-2 33 2005 Qualification concept for lifetime assessment of PE pressure pipes for arbitrary installation conditions
Lang 2006 Proceedings Plastic Pipes XIII A novel qualification concept for lifetime and safety assessment of PE pressure pipes for arbitrary installation conditions
Haager 2006 Fracture Mechanics Methods for the Accelerated Characterization of the Slow Crack Growth Behavior of Polyethylene Pipe Materials
Polym. Test Pinter 26 2 180 2007 10.1016/j.polymertesting.2006.09.010 Influence of nonylphenol-polyglycol-ether environments on the results of the full notch creep test
Frank vol. 4 2169 2009 Lifetime prediction of polyethylene pipes based on an accelerated extrapolation concept for creep crack growth with fatigue tests on cracked round bar specimens
Eng. Fract. Mech. Frank 76 2780 2009 10.1016/j.engfracmech.2009.06.009 A fracture mechanics concept for the accelerated characterization of creep crack growth in PE-HD pipe grades
Polym. Test. Frank 28 737 2009 10.1016/j.polymertesting.2009.06.004 Prediction of the remaining lifetime of polyethylene pipes after up to 30 years in use
Frank 2010 Fracture Mechanics Based Lifetime Assessment and Long-term Failure Behavior of Polyethylene Pressure Pipes
Eng. Fract. Mech. Huta 78 17 3049 2011 10.1016/j.engfracmech.2011.09.001 A numerical methodology for lifetime estimation of HDPE pressure pipes
Eng. Fract. Mech. Huta 108 98 2013 10.1016/j.engfracmech.2013.04.014 The effect of residual stress on polymer pipe lifetime
Pinter 2010 Proceedings Pipes XV, Vancouver, Canada Cyclic CRB tests - a quick and reliable tool for ranking of PE pipe grades
Frank 2010 Proceedings Pipes XV, Vancouver, Canada Fracture mechanics lifetime prediction of PE 80 and PE 100 pipes under complex loading conditions
Frank vol. 3 2214 2011 Characterization of crack initiation and slow crack growth in polyethylene with cyclic cracked round bar tests
Macromol. Symp. Redhead 311 1 41 2012 10.1002/masy.201000110 Analysis of molecular and morphological effects on slow crack growth in modern PE pipe grades by cyclic fracture mechanics tests
Macromol. Symp. Frank 311 1 103 2012 10.1002/masy.201000097 Investigation of the slow crack growth behavior of static and cyclic loaded specimens of polyethylene by 2D and 3D optical fracture surface analysis
Eng. Fract. Mech. Redhead 101 2 2013 10.1016/j.engfracmech.2012.09.022 Investigation of slow crack growth initiation in polyethylene pipe grades with accelerated cyclic tests
Frank vol. 3 1899 2012 The influence of test frequency and eccentric crack growth on cyclic CRB tests
Frank 2012 Proceedings Plastic Pipes XVI, Barcelona, Spain Accelerated material testing with cyclic CRB tests
Macromol. Symp. Frank 311 1 112 2012 10.1002/masy.201000096 Numerical assessment of PE 80 and PE 100 pipe lifetime based on Paris-Erdogan equation
Frank 2012 Proceedings Plastic Pipes XVI, Barcelona, Spain Comparison of Accelerated Tests for PE Grades Lifetime Assessment
ONR 25194 2011 Determination of the Resistance to Slow Crack Growth of Polyethylene with Cracked Round Bar (CRB) Specimens
J. Mech. Ph. Solid. Dugdale 8 100 1960 10.1016/0022-5096(60)90013-2 Yielding of steel sheets containing slits
Lustiger 305 1986 Failure of Plastics Environmental stress cracking: the phenomenon and its utility
J. Macromol. Sci. Phys. Kausch 38 5/6 803 1999 10.1080/00222349908248140 Crazing in semicrystalline thermoplastics
Kausch 1987 Polymer Fracture
J. Macromol. Sci. Phys. Lustiger 29 1047 1991 An analytical technique for measuring relative tie-molecule concentration in polyethylene
Angew. Makromol. Chem. Lang 247 131 1997 10.1002/apmc.1997.052470109 Applicability and limitations of current lifetime prediction models for thermoplastics pipes under internal pressure
J. Appl. Polym. Sci. Pinter 90 3191 2003 10.1002/app.12944 Effect of stabilization on creep crack growth in high-density polyethylene
Macromol. Symp. Pinter 217 307 2004 10.1002/masy.200451327 Thermo-oxidative degradation during creep crack growth of PE-HD grades as assessed by FT-IR spectroscopy
J. Appl. Mech. Irwin 24 361 1957 10.1115/1.4011547 Analysis of stresses and strains near the end of a crack traversing a plate
Hertzberg 1980 Fatigue of Engineering Plastics
Kinloch 1983 Fracture Behaviour of Polymers
Lang 1984 Applicability of Linear Elastic Fracture Mechanics to Fatigue in Polymers and Short-fiber Composites
Broek 1986 Elementary Engineering Fracture Mechanics
Williams 1987 Fracture Mechanics of Polymers
Hertzberg 1989 Deformation and Fracture Mechanics of Engineering Materials
J. Mater. Sci. Parsons 34 3315 1999 10.1023/A:1004616728535 Correlation of stepwise fatigue and creep slow crack growth in high density polyethylene
Anderson 2005 Fracture Mechanics - Fundamentals and Application
Murakami 1990 Stress Intensity Factors Handbook
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.