Conventional ships generated almost no cavitation erosion because they traveled at low speed. Thus, most ships have used painting, ICCP and sacrificial anode system. However, with the activation of international trading, and the increase of low-price, large-volume cargos, ships are becoming larger a...
Conventional ships generated almost no cavitation erosion because they traveled at low speed. Thus, most ships have used painting, ICCP and sacrificial anode system. However, with the activation of international trading, and the increase of low-price, large-volume cargos, ships are becoming larger and faster. As a result, damages due to cavitations and corrosions have accelerated. Cavitation and erosion corrosions cause damages to materials by physical shock waves generated from the collapse of bubbles which are generated when the moving parts rotate in seawater. The stern in particular is exposed to more severe environment due to cavitation and high flow speed. When cavitation and electrochemical damages are combined with exposure to severe environment, it has serious impact on the life span of equipment. Therefore, this study investigated the electrochemical and cavitation characteristics in sea environment for Zn primer coating which is a pretreatment process of painting for rudders for ships. As a result, corrosion resistance improved, but erosion resistance did not.
Conventional ships generated almost no cavitation erosion because they traveled at low speed. Thus, most ships have used painting, ICCP and sacrificial anode system. However, with the activation of international trading, and the increase of low-price, large-volume cargos, ships are becoming larger and faster. As a result, damages due to cavitations and corrosions have accelerated. Cavitation and erosion corrosions cause damages to materials by physical shock waves generated from the collapse of bubbles which are generated when the moving parts rotate in seawater. The stern in particular is exposed to more severe environment due to cavitation and high flow speed. When cavitation and electrochemical damages are combined with exposure to severe environment, it has serious impact on the life span of equipment. Therefore, this study investigated the electrochemical and cavitation characteristics in sea environment for Zn primer coating which is a pretreatment process of painting for rudders for ships. As a result, corrosion resistance improved, but erosion resistance did not.
참고문헌 (14)
10.1016/j.wear.2005.08.001 S. Hattori, Y. Goto and T. Fukuyama: Wear Vol. 260(2006), p.1212.
J. H. Hwang and U. J. Lim: J. Corro Sci. Soc. of Korea Vol. 25(1)(1996), p.317.
J. M. Han, D. S. Kong, I. H. Song and C. S. Lee: Analysis of the cavitating flow around the horn-type rudder in the race of a propeller, CAV2001, 2001, session B9. 005, 1.
H. I. Lee, M. S. Han, K. K. Baek, C. H. Lee, C. S. Shin and M. K. Chung: Corros. Sci. Tech. Vol. 7(5) (2008), p.274.
Tretheway, K. R., Chamberlain, J., Corrosion, 1988, 153.
M. G. Talks, G. Moreton, Cavitation Erosion Fluid System, Proc. ASME Symp., 1981, 139.
S. J. Kim, D. H. Kim, M. H. Lee, K. J. Kim and K. M. Moon: The Korean Society of Ocean Engineers Vol. 14(2) (2000), p.106.
Y. T. Kho: J. Corro Sci. Soc. of Korea Vol. 27(5)(1998), p.563.
S. J. Kim and S. J. Lee: Corrosion Science and Technology Vol. 10(3) (2011), p.101.
J. J. Kim, J. S. Park and S. B. Jeon: J. Corrs. Sci. Soc. of Korea Vol. 20(2) (1991), p.132.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.