[논문]Wet spinning of PVA composite fibers with a large fraction of multi-walled carbon nanotubes

Lai, D.; Wei, Y.; Zou, L.; Xu, Y.; Lu, H.

doi:10.1016/j.pnsc.2015.10.003

Wet spinning of PVA composite fibers with a large fraction of multi-walled carbon nanotubes 원문보기

Progress in natural science : communication of state key laboratories of China, v.25 no.5, 2015년, pp.445 - 452

Lai, D. , Wei, Y. , Zou, L. , Xu, Y. , Lu, H.

Abstract ▼ AI-Helper

PVA composites fibers with a large fraction of multi-walled carbon nanotubes modified by both covalent and non-covalent functionalization were produced by a wet-spinning process. Model XQ-1 tensile tester, thermogravimetric analysis, scanning electron microscopy, differential scanning calorimetry, and wide-angle X-ray diffraction were used to characterize the properties of PVA/MWNT composite fibers. The TGA results suggested that MWNTs content in composite fibers were ranged from 5.3wt% to 27.6wt%. The mechanical properties of PVA/MWNT composite fibers were obviously superior to pure PVA fiber. The Young@?s modulus of composite fibers enhanced with increasing the content of MWNTs, and it rised gradually from 6.7GPa for the pure PVA fiber to 12.8GPa for the composite fibers with 27.6wt% MWNTs. Meanwhile, the tensile strength increased gradually from 0.39GPa for the pure PVA fiber to 0.74GPa for the composite fibers with 14.4wt% MWNTs. Nevertheless, the tensile strength of the composite fibers decreased as the MWNTs content up to 27.6wt%. SEM results indicated that the MWNTs homogeneously dispersed in the composite fibers, however some agglomerates also existed when the content of MWNTs reached 27.6wt%. DSC results proved strong interfacial interaction between MWNTs and PVA chain, which benefited composite fibers in the efficient stress-transfer. WXAD characterization showed that the orientation of PVA molecules declined from 94.1% to 90.9% with the increasing of MWNTs content. The good dispersibility of MWNTs throughout PVA matrix and efficient stress-transfer between MWNTs and PVA matrix may contributed to significant enhancement in the mechanical properties.

주제어

참고문헌 (25)

Nature Iijima 354 6348 56 1991 10.1038/354056a0

상세보기
Nature Dalton 423 6941 703 2003 10.1038/423703a

상세보기
Polymer Sandler 44 19 5893 2003 10.1016/S0032-3861(03)00539-1

상세보기
Carbon Zhang 45 9 1917 2007 10.1016/j.carbon.2007.05.007

상세보기
J. Phys. Chem. A Dyke 108 51 11151 2004 10.1021/jp046274g

상세보기
Chem. Sci. Clave 2 10 1887 2011 10.1039/c1sc00342a

상세보기
Nano Lett. Zhang 3 9 1285 2003 10.1021/nl034336t

상세보기
Carbon Li 46 5 829 2008 10.1016/j.carbon.2008.02.022

상세보기
Macromolecules Moniruzzaman 39 16 5194 2006 10.1021/ma060733p

상세보기
Polymer Potschke 46 23 10355 2005 10.1016/j.polymer.2005.07.106

상세보기
Int. J. Polym. Mater. Anand 59 6 438 2010 10.1080/00914030903538587

상세보기
Macromol. Res. Jee 20 6 650 2012 10.1007/s13233-012-0094-2

원문보기 상세보기
Int. J. Pharm. Suhrenbrock 412 1-2 28 2011 10.1016/j.ijpharm.2011.03.061

상세보기
J. Alloy. Compd. Stobinski 501 1 77 2010 10.1016/j.jallcom.2010.04.032

상세보기
Mater. Charact. Scheibe 61 2 185 2010 10.1016/j.matchar.2009.11.008

상세보기
J. Solid State Chem. Yu 181 3 432 2008 10.1016/j.jssc.2007.12.017

상세보기
J. Appl. Polym. Sci. Fu 128 2 1044 2013 10.1002/app.38260

상세보기
Chem. Mater. Szabo 18 11 2740 2006 10.1021/cm060258+

상세보기
Carbon Datsyuk 46 6 833 2008 10.1016/j.carbon.2008.02.012

상세보기
Appl. Phys. A - Mater. Sci. Process. Xu 100 2 379 2010 10.1007/s00339-010-5849-z

상세보기
Nano Lett. Wei 6 8 1627 2006 10.1021/nl0605770

상세보기
Macromol. Chem. Phys. Minus 210 21 1799 2009 10.1002/macp.200900223

상세보기
Polymer Chae 47 10 3494 2006 10.1016/j.polymer.2006.03.050

상세보기
Nanoscale Kou 5 10 4370 2013 10.1039/c3nr00455d

상세보기
Fiber Polym. Wang 7 4 323 2006 10.1007/BF02875761

원문보기 상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Wet spinning of PVA composite fibers with a large fraction of multi-walled carbon nanotubes 원문보기

Abstract ▼ AI-Helper

주제어

참고문헌 (25)

이 논문을 인용한 문헌

관련 콘텐츠

원문 보기

원문 URL 링크

오픈액세스(OA) 유형

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트