NTIS 바로가기International journal of fatigue, v.88, 2016년, pp.142 - 155
Huter, P. , Oberfrank, S. , Grun, F. , Stauder, B.
In this paper, different hypo-eutectic Al-Si cast alloys with varying silicon, copper and iron contents were tested under thermo-mechanical fatigue (TMF) conditions to achieve a unified approach to damaging and fatigue endurance behaviour. The cylinder heads from which the specimens were taken were ...
Int J Fatigue Tabibian 53 0 75 2013 10.1016/j.ijfatigue.2012.01.012 TMF-LCF life assessment of a lost foam casting {A319} aluminum alloy
Proc Eng Grieb 2 1 1767 2010 10.1016/j.proeng.2010.03.190 Thermomechanical fatigue of cast aluminium alloys for cylinder head applications - experimental characterization and life prediction
Ceram Int Azadi 39 8 9099 2013 10.1016/j.ceramint.2013.05.006 Experimental fatigue lifetime of coated and uncoated aluminum alloy under isothermal and thermo-mechanical loadings
Proc Eng Tsuyoshi-Takahashi 2 1 767 2010 10.1016/j.proeng.2010.03.083 Low cycle thermal fatigue of aluminium alloy cylinder head in consideration of changing metrology microstructure
Kohler 1998 Verbrennungsmotoren
Zolotorevsky 2007 Casting aluminium alloys
Loehe 161 2003 Fifth international conference on low cycle fatigue Important aspects of cyclic deformation, damage and lifetime behaviour in thermomechanical fatigue of engineering alloys
Mater Des Azadi 66 Part B, 0 587 2015 10.1016/j.matdes.2014.04.022 Damage prediction for un-coated and coated aluminum alloys under thermal and mechanical fatigue loadings based on a modified plastic strain energy approach
ASM Int Sehitoglu 1 527 1996 Thermal and thermomechanical fatigue of structural alloys
Int J Fatigue Gocmez 32 4 769 2010 10.1016/j.ijfatigue.2009.11.003 A new low cycle fatigue criterion for isothermal and out-of-phase thermomechanical loading
Koberl H. Entwicklung eines modells zur beschreibung des lebensdauerverhaltens von ne-legierungen (al, cu, ni) unter thermomechanischer beanspruchung, Ph.D. Thesis, Montanuniversitat Leoben; 2008.
RMZ - Mater Geoenviron Kores 55 3 307 2008 Aluminium alloys for cylinder heads
Proc Eng Mattos 2 1 759 2010 10.1016/j.proeng.2010.03.082 Fatigue properties and micromechanism of fracture of an AlSiMg0.6 cast alloy used in diesel engine cylinder head
Mater Sci Eng: A Chan 341 12 18 2003 10.1016/S0921-5093(02)00196-X Fatigue crack growth and fracture paths in sand cast {B319} and {A356} aluminum alloys
Trans Nonferr Metals Soc China Zeren 21 8 1698 2011 10.1016/S1003-6326(11)60917-5 Influence of Cu addition on microstructure and hardness of near-eutectic Al-Si-xCu-alloys
Int J Sci Res Pub Rana 2 1 2012 Reviews on the influences of alloying elements on the microstructure and mechanical properties of aluminium alloys and aluminium alloy composites
Mohamed 55 2012 Heat treatment - conventional and novel applications A review on the heat treatment of Al-Si-Cu/Mg casting alloys
Mater Des Azadi 45 0 279 2013 10.1016/j.matdes.2012.08.066 Heat treatment effect on thermo-mechanical fatigue and low cycle fatigue behaviors of a356.0 aluminum alloy
ASM Int Handbook 4 1 72 1991 Heat treating
Kaufman 2000 Introduction to aluminum alloys and tempers
Int J Fatigue Huter 82 Part 3 588 2016 10.1016/j.ijfatigue.2015.09.015 High- and low-cycle fatigue influence of silicon, copper, strontium and iron on hypo-eutectic Al-Si-Cu and Al-Si-Mg cast alloys used in cylinder heads
Mater Sci Eng: A Huter 618 0 578 2014 10.1016/j.msea.2014.08.062 Comparison of microstructural crack paths between hypo-eutectic Al-Si-Cu and Al-Si-Mg cast alloys in high plasticity regimes under rotating bending
Light Metal Age Benedyk 1 16 2010 International temper designation systems for wrought aluminum alloys
Altenpohl Vol. 5 2005
Shackelford Vol. 7 2005
ISO. Metallic materials - fatigue testing - strain-controlled thermomechanical fatigue testing method. In: ISO 12111:2011, International Organization for Standardization, Geneva, Switzerland; 2011.
Stauder vol. 2122 2011
Rafetzeder M. Vergleich des waermebehandlungsverhaltens von g-AlSi8Cu3 primaer- und sekundaerlegierungen. Master’s thesis, FH Material- und Verarbeitungstechnik Wels; 2007.
Mater Test Bischoff 54 10 655 2012 10.3139/120.110384 Innovative pruefmethodik zur ermittlung der thermomechanischen ermudung an zylinderkopfen
Barlas B. Etude du comportement et de lendommagement en fatigue dalliages daluminium de fonderie. Ph.D. Thesis, Ecole des Mines de Paris; 2004.
Mater Sci Eng: A Firouzdor 454455 528 2007 10.1016/j.msea.2007.01.018 Effect of microstructural constituents on the thermal fatigue life of {A319} aluminum alloy
Int J Fatigue Charkaluk 63 127 2014 10.1016/j.ijfatigue.2014.01.017 Probability density functions: from porosities to fatigue lifetime
Int J Fatigue Bose-Filho 29 9-11 1846 2007 10.1016/j.ijfatigue.2007.01.006 Al-Si cast alloys under isothermal and thermomechanical fatigue conditions
Michelfeit S. Werkstoffgesetze einer AlSi-gusslegierung unter hochtemperaturbeanspruchung in abhangigkeit des werkstoffzustandes. Ph.D. Thesis, Technische Universitat Darmstadt; 2012.
Thalmair S. Thermomechanische ermudung von aluminium-silizium-gusslegierungen unter ottomotorischen beanspruchungen. Ph.D. Thesis, Universitat Karlsruhe; 2009.
Metall Mater Trans A Sudha 44a 2358 2013 The fracture characteristics of a near eutectic Al-Si based alloy under compression
Int J Fatigue Payne 32 2 247 2010 10.1016/j.ijfatigue.2009.06.003 Observations of fatigue crack initiation in 7075-T651
Metall Mater Trans A: Gall 30A 3079 1999 10.1007/s11661-999-0218-2 The debonding and fracture of si particles during the fatigue of a cast Al-Si alloy
Acta Mater Lados 54 6 1475 2006 10.1016/j.actamat.2005.11.019 Fatigue crack growth mechanisms at the microstructure scale in Al-Si-Mg cast alloys: mechanisms in the near-threshold regime
Raninger P. Numerical studies on crack arrays in aluminum pressure die casting molds. Master’s thesis, Montanuniversitaet Leoben; 2009.
Nucl Eng Des Haddar 235 9 945 2005 10.1016/j.nucengdes.2004.12.005 2d simulation of the initiation and propagation of crack array under thermal fatigue
Int J Solids Struct Haddar 42 2 771 2005 10.1016/j.ijsolstr.2004.06.033 Thermal fatigue crack networks: an computational study
Metall Mater Trans A Lados 37 8 2405 2006 10.1007/BF02586215 Fatigue crack growth mechanisms at the microstructure scale in Al-Si-Mg cast alloys: mechanisms in regions II and III
Riedler M. Methodikfindung zur simulation von thermomechanisch beanspruchten motorbauteilen aus aluminiumlegierungen. Ph.D. Thesis, Montanuniversitat Leoben; 2005.
Timpel M. Einfluss von strontium auf die mikrostruktur von aluminium-silizium legierungen. Ph.D. Thesis, Technischen Universitat Berlin, b83, June 2012.
J Light Met Makhlouf 1 4 199 2001 10.1016/S1471-5317(02)00003-2 The aluminum-silicon eutectic reaction: mechanisms and crystallography
J Alloys Comp Kumari 460 1-2 472 2008 10.1016/j.jallcom.2007.05.085 Structure and properties of calcium and strontium treated Al-7Si-0.3Mg alloy: a comparison
Int J Fatigue Dezecot 77 0 154159 2015 Microstructural characterization and high cycle fatigue behavior of investment cast {A357} aluminum alloy
J Alloys Comp Joseph 625 0 296 2015 10.1016/j.jallcom.2014.10.207 Stress states in individual Ai particles of a cast Al-Si alloy: micro-raman analysis and microstructure based modeling
Acta Mater Harris 55 5 1681 2007 10.1016/j.actamat.2006.10.028 Application of the raman technique to measure stress states in individual Si particles in a cast Al-Si alloy
Trans Am Foundry Soc Ma 112 2 04 2004 Effect of iron and cooling rate on tensile properties of b319.2 (AlSi6Cu4) Al-alloy in non-modified and Sr-modified conditions
Mater Trans Cao 47 5 1303 2006 10.2320/matertrans.47.1303 Morphology of beta-Al5FeSi phase in Al-Si cast alloys
Mater Des Goswami 22 3 199 2001 10.1016/S0261-3069(00)00060-1 Dwell effects on high temperature fatigue behavior: Part I
Mater Des Goswami 22 3 217 2001 10.1016/S0261-3069(00)00061-3 Dwell effects on high temperature fatigue damage mechanisms: Part {II}
Mater Sci Eng: A Moverare 528 29-30 8660 2011 10.1016/j.msea.2011.08.027 Hold-time effect on the thermo-mechanical fatigue crack growth behaviour of Inconel 718
Minichmayr vol. 14 1115 2005 Euromat 2005 The influence of superimposed high-cycle-fatigue loading on the thermo-mechanical-fatigue life
Luft J. Thermisch mechanische und ueberlagerte thermisch-mechanische mechanische ermuedungsbeanspruchung der zylinderkopflegierungen AlSi7Mg und AlSi5Cu3. Ph.D. Thesis, Universitat Karlsruhe; 2007.
Winter G. Thermomechanische ermudung des gusseisenwerkstoffes gjv450. Ph.D. Thesis, Montanuniversitat Leoben; 2008.
Ostermann vol. 2 2007
Corrosion Troutner 15 1 25 1959 10.5006/0010-9312-15.1.25 Observations on the mechanisms and kinetics of aqueous aluminum corrosion (Part 1-role of the corrosion product film in the uniform aqueous corrosion of aluminium)
J Electrochem Soc Smeltzer 103 4 209 1956 10.1149/1.2430279 Oxidation of aluminum in the temperature range 400-600 c
Davis 1999 Corrosion of aluminum and aluminum alloys
Vargel 2004 Corrosion of aluminium
Mater Res Santos 8 2 155 2005 10.1590/S1516-14392005000200011 Corrosion performance of Al-Si-Cu hypereutectic alloys in a synthetic condensed automotive solution
Am Foundrymen’s Soc Backerud 2 266 1990 Solidification characteristics of aluminum alloys
Trans Nonferrous Met Soc China Zeng 21 12 2559 2011 10.1016/S1003-6326(11)61092-3 Corrosion mechanism associated with Mg2Si and Si particles in Al-Mg-Si alloys
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.