[논문]Phase transformation under thermal fatigue of high Mn-TWIP steel: Microstructure and mechanical properties

Roa, J.J.; Besharatloo, H.; Fargas, G.; Calvo, J.; Mateo, A.

doi:10.1016/j.msea.2016.09.046

Phase transformation under thermal fatigue of high Mn-TWIP steel: Microstructure and mechanical properties 원문보기

Materials science & engineering. properties, microstructure and processing. A, Structural materials, v.677, 2016년, pp.431 - 437

Roa, J.J. , Besharatloo, H. , Fargas, G. , Calvo, J. , Mateo, A.

Abstract ▼ AI-Helper

High Mn steels present both high tensile strength and good ductility, therefore they have attracted attention as promising candidates for the next-generation of automotive steels. However, slight changes during the manufacturing process or in service conditions (i.e. chemical composition, annealing temperature, among others) can promote significant variations in their microstructure, leading to a strong modification in their mechanical response. In this regard, this paper discusses the relationship between the different microstructures generated on a high Mn-twinning induced plasticity (TWIP) steel and its mechanical properties evaluated by means of Vickers's hardness, tensile testing and also high cycle fatigue response. Different conditions, namely: as received, annealed at 500oC and thermally cycled at 500oC during 15, 36, 56 and 75 cycles, have been analyzed. The results exhibit the development of a heterogeneous pearlitic microstructure with a plateau on its fraction content and Vickers's hardness at ~24% and 292+/-5HV, respectively, after 36 thermal fatigue cycles. Finally, pearlite colonies have been nucleated during the thermal fatigue treatment along the austenitic grain boundary producing a deleterious effect on the tensile and high cycle fatigue behavior.

주제어

참고문헌 (44)

Acta Mater. Bracke 57 1512 2009 10.1016/j.actamat.2008.11.036

상세보기
ISIJ Int. Frommeyer 43 438 2003 10.2355/isijinternational.43.438

상세보기
Int. J. Plast. Grassel 16 1391 2000 10.1016/S0749-6419(00)00015-2

상세보기
Mater. Sci. Eng. A Barbier 500 196 2009 10.1016/j.msea.2008.09.031

상세보기
Acta Mater. Curtze 58 5129 2010 10.1016/j.actamat.2010.05.049

상세보기
J. Mater. Sci. Technol. De Cooman 28 513 2012 10.1179/1743284711Y.0000000095

상세보기
Metall. Mater. Trans. A Saced-Akbari 2012 43 1688
Scr. Mater. Saced-Akbari 66 1024 2012 10.1016/j.scriptamat.2011.12.041

상세보기
J. Phys. IV Kruger 110 189 2003
Mater. Sci. Eng. A Allain 387-389 158 2004 10.1016/j.msea.2004.01.059

상세보기
Mater. Sci. Eng. A Oh 197 147 1995 10.1016/0921-5093(94)09751-8

상세보기
Acta Mater. Vercammen 2004 52 2005
J. Iron Steel Res. Int. Ding 13 66 2006 10.1016/S1006-706X(06)60113-1

상세보기
Mater. Sci. Eng. A Allain 387-389 272 2004 10.1016/j.msea.2004.05.038

상세보기
Acta Mater. Jin 2012 60 1680
Mater. Des. Dini 31 3395 2010 10.1016/j.matdes.2010.01.049

상세보기
Arch. Mater. Sci. Eng. Dobrzanski 2 69 2009
Mater. Sci. Eng. A Song 610 145 2014 10.1016/j.msea.2014.05.033

상세보기
Mater. Sci. Eng. A Zhao 608 106 2014 10.1016/j.msea.2014.04.084

상세보기
J. Iron Steel Res. Int. Hua 13 66 2006 10.1016/S1006-706X(06)60113-1

상세보기
J. Achiev. Mater. Manuf. Eng. Dobrzanski 55 230 2012
J. Iron Steel Res. Int. Wu 21 352 2014 10.1016/S1006-706X(14)60054-6

상세보기
Mater. Sci. Eng. A Guo 584 133 2013 10.1016/j.msea.2013.07.020

상세보기
Mater. Sci. Eng. A Kim 528 4696 2011 10.1016/j.msea.2011.02.068

상세보기
Mater. Sci. Eng. A Hamada 517 68 2009 10.1016/j.msea.2009.03.039

상세보기
Mater. Sci. Eng. A Hamada 527 5715 2010 10.1016/j.msea.2010.05.035

상세보기
W. D. Callister, Introduccion a la ciencia e ingenieria de los materiales. Reverte, 2002, vol. 1. ISBN : 8429172521.
Acta Mater. Xiao 54 1265 2006 10.1016/j.actamat.2005.10.055

상세보기
Acta Mater. van Tol 64 33 2014 10.1016/j.actamat.2013.10.037

상세보기
FSstel database, in: 〈www.factsage.com〉 (visited 08/09/2016).
Calphad Bale 33 295 2009 10.1016/j.calphad.2008.09.009

상세보기
ASTM E8-04: Standard Test Methods for Tension Testing of Metallic Material, 2008.
Mater. Test. Mateo 57 136 2015 10.3139/120.110686

상세보기
ASTM E466-96. Standard Practice for Conducting force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Materials, 2002.
Collins 369 1981 Failure of Materials in Mechanical Design
MRS Bull. Raabe 35 982 2010 10.1557/mrs2010.703

상세보기
Acta Mater. Li 59 3965 2011 10.1016/j.actamat.2011.03.022

상세보기
ISIJ Int. Chen 2007 47 1804
Int. J. Plast. Shickhelsouk 25 105 2009 10.1016/j.ijplas.2007.11.004

상세보기
Metall. Trans. A Dastur 12A 749 1981 10.1007/BF02648339

상세보기
Acta Metall. Cuddy 20 1157 1972 10.1016/0001-6160(72)90164-2

상세보기
Metall. Mater. Trans. A Adler 17A 1725 1986 10.1007/BF02817271

상세보기
Mater. Charact. De Almeida 41 137 1998 10.1016/S1044-5803(98)00031-X

상세보기
Mater. Sci. Eng. A Roa 628 410 2015 10.1016/j.msea.2015.01.043

상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Phase transformation under thermal fatigue of high Mn-TWIP steel: Microstructure and mechanical properties 원문보기

Abstract ▼ AI-Helper

주제어

참고문헌 (44)

이 논문을 인용한 문헌

관련 콘텐츠

원문 보기

원문 URL 링크

오픈액세스(OA) 유형

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트