NTIS 바로가기Polymer testing, v.55, 2016년, pp.101 - 108
Bae, H. , Lee, K. , Pyo, S. , Choi, S.
Slow crack growth behavior in polyethylene pipe grade resins were studied using both static fatigue (stress-rupture) and cyclic fatigue tests. This was done to better understand the applicability of cyclic fatigue in the prediction of slow crack growth ranking determined from the static fatigue test...
Polymer Lustiger 24 12 1647 1983 10.1016/0032-3861(83)90187-8 Importance of tie molecules in preventing polyethylene fracture under long-term loading conditions
J. Mater. Sci. Brown 20 12 4553 1985 10.1007/BF00559346 The initiation of slow crack growth in linear polyethylene under single edge notch tension and plane strain
Polymer Brown 36 3 543 1995 10.1016/0032-3861(95)91563-M A fundamental theory for slow crack growth in polyethylene
Polym. Eng. Sci. Brown 47 4 477 2007 10.1002/pen.20696 Intrinsic lifetime of polyethylene pipelines
Polym. Eng. Sci. Nishimura 31 6 399 1991 10.1002/pen.760310603 Fatigue behavior of medium-density polyethylene pipes
Polymer Ward 32 12 2172 1991 10.1016/0032-3861(91)90043-I The mechanism of slow crack growth in polyethylene by an environmental stress cracking agent
Polym. Test. Pyo 30 3 324 2011 10.1016/j.polymertesting.2010.12.002 Utilization of notched ring test for larger diameter pipes and fittings
Macromol. Symp. Tischler 296 1 626 2010 10.1002/masy.201051082 Notched ring test for measuring slow cracking resistance in plastics pipes and fittings
Plast. Rubber Compos. Macromol. Eng. Beech 34 7 294 2005 10.1179/174328905X59791 Interpretation of results of full notch creep test and comparison with notched pipe test
Polymer Kurelec 46 6369 2005 10.1016/j.polymer.2005.05.061 Strain hardening modulus as a measure of environmental stress crack resistance of high density polyethylene
Proc. Plast. Pipe van der Stok XVI 2012 Strain hardening test on PE pipe materials
Polym. Test. Pinter 26 2 180 2007 10.1016/j.polymertesting.2006.09.010 Cyclic crack growth tests with CRB specimens for the evaluation of the long-term performance of PE pipe grades
Polym. Test. Frank 33 161 2014 10.1016/j.polymertesting.2013.11.013 Cyclic cracked round bar test: final results of international round robin test
Vinogradov 159 2001 Cyclic Loading Effects on Durability of Polymer Systems, Long Term Durability of Structural Materials Durability
Li 2011 Report No. ANL-ARC-186
Nucl. Eng. Tech. Park 38 3 293 2006 Evaluation and test of a crack initiation for a 316 SS cylindrical Y-junction structure in a liquid metal reactor
Polym. Eng. Sci. Bowman 26 22 1582 1986 10.1002/pen.760262209 A methodology for describing creep-fatigue interactions in thermoplastic components